The invention provides a flange forging steel material and its production process, the proportion of the chemical composition of the material: C:0.13-0.20; Si:0.20-0.60; Mn:1.20-1.60; P: = 0.030; S: = 0.030; Cr: = 0.25; Cu: = 0.25; Ni = 0.25, electroslag remelting method in the smelting process, the quenching temperature of 935 DEG C plus or minus 10 DEG C, the tempering temperature is 670 DEG C - 10 DEG C for heat treatment, the invention provides a hydrogen resistant steel flange forgings, P and S, Ni reduced the proportion of chemical components, in the smelting process by electroslag remelting, improve the material purity, the heat treatment process by normalizing and tempering the strength and hardness of process control to the standard value near the lower limit, effectively improve the performance of anti hydrogen materials.
【技术实现步骤摘要】
一种抗氢钢材质的法兰锻件及其生产工艺
本专利技术主要涉及金属锻造领域，尤其涉及一种抗氢钢材质的法兰锻件及其生产工艺。
技术介绍
近些年，随着设计标准不断提高和人们安全意识的不断增强，在石油化工领域和其它工作于酸性环境中的设备锻件，抗氢钢使用量越来越大。抗氢钢是抗氢致开裂用钢的简称，氢致裂纹（HIC）作为一种缺陷存在于锻件中，其对使用性能的影响目前尚无全面的认识，但大量研究表明，氢致裂纹对材料的强度指标影响不大，但对韧性指标影响比较大，会增大材料脆性倾向，这种缺陷曾给世界各国造成了很多突发事故，带来严重损失。目前石油化工中很多锻件，尤其是表面与酸性介质接触的锻件，或其他行业临氢工况的锻件，在订货中多数都有对材料的抗氢要求。
技术实现思路
本专利技术提供一种抗氢钢材质的法兰锻件，其材料中各化学成分比重为：C:0.13-0.20；Si:0.20-0.60；Mn：1.20-1.60；P:≤0.030；S:≤0.030；Cr:≤0.25；Cu:≤0.25；Ni≤0.25。本专利技术还提供了用于生产上述抗氢性能高的钢材质的法兰锻件的生产工艺，包括冶炼、锻造、热处理，所述热处理包括...
【技术保护点】
一种抗氢钢材质的法兰锻件，其特征在于：其材料中各化学成分比重为：C:0.13‑0.20；Si:0.20‑0.60；Mn ：1.20‑1.60 ；P:≤ 0.030；S:≤ 0.030；Cr: ≤ 0.25；Cu:≤ 0.25；Ni≤ 0.25。
【技术特征摘要】
1.一种抗氢钢材质的法兰锻件，其特征在于：其材料中各化学成分比重为：C:0.13-0.20；Si:0.20-0.60；Mn：1.20-1.60；P:≤0.030；S:≤0.030；Cr:≤0.25；Cu:≤0.25；Ni≤0.25。2.一种用于权利要求1所述的抗氢钢材质的法兰锻件的生产工艺，包括冶炼、锻造、热处理，其特征在于：冶炼采用电渣重熔方法。3.根据权利要求2...
【专利技术属性】
技术研发人员：许建平，
申请(专利权)人：无锡市法兰锻造有限公司，
类型：发明
国别省市：江苏,32