A preparation method of ultrafine GCC coating slurry, which is characterized in that: firstly, heavy calcium carbonate powder pulping, ultra-fine grinding, grinding to which is less than 2 m in 80 ~ 90%. The heavy calcium carbonate slurry diluted into the weight content of 10%, and then the slurry is fed into the horizontal spiral discharge centrifugal classifier in classification processing, collection of small particle size, large particles slurry return to the stripping machine for further grinding, adding ammonium carbonate to small particles in the slurry, adding amount of ammonium carbonate as heavy calcium carbonate powder weight 1%, after mixing evenly into the filter, filter, filter cake collection, filter cake with sodium polyacrylate dispersing agent was dispersed, sodium polyacrylate dispersing agent was added heavy calcium carbonate powder weight 1%, coated superfine heavy calcium sizing agent.
【技术实现步骤摘要】
一种超细涂布重钙浆料的制备方法
本专利技术涉及一种超细涂布重钙浆料的制备方法。
技术介绍
造纸中加入填料可以提高纸张的不透明度和亮度，改进纸张的平滑度和均匀状态，增加纸张的柔软性，降低纸张的吸湿性和变形程度，同时还有利于降低生产成本。钛白粉有高的折光率和散射系数，是很好的造纸填料，但由于其价格昂贵，一般只用于高档薄页印刷纸，以提高纸张的不透明度；而碳酸钙由于其价格低廉，且同样能提高纸张的不透明度、增加纸张的吸油墨性能，作为造纸填料具有一定的成本优势。随着酸性造纸向中性造纸转变，碳酸钙日益成为中国造纸工业提高纸张质量、降低造纸成本的重要原材料。重钙与轻钙在纸张中的应用效果有较大的差别：轻钙与重钙所抄纸样白度相差不大，两者的白度均较高；但在不透明度方面，轻钙所抄纸样的不透明度较高，加入轻钙后可以提高纸页的不透明度。用轻钙所抄纸样其松厚度明显高于重钙；轻钙的平均粒径较重钙小，相应地具有更大的比表面积，对AKD施胶剂的吸附作用比重钙强，因而AKD施胶剂的用量比重钙大。在相同填料用量时，轻钙比重钙的灰分高，主要是由于重钙的粒径小，在纸页脱水成形时，纤维对细小颗粒截留差；而轻...
【技术保护点】
一种超细涂布重钙浆料的制备方法，其特征在于：首先将重质碳酸钙粉制浆，将重质碳酸钙粉加入水中，并向水中加入聚丙烯酸钠分散剂，聚丙烯酸钠分散剂加入量为重质碳酸钙干粉重量的1.0%，搅拌均匀配成重质碳酸钙浆料，重质碳酸钙浆料的重量含量为50%，然后采用湿式超细剥片机对重质碳酸钙进行超细磨，制得重质碳酸钙浆料，其中小于2µm含量80～90%；将重量含量为50%的重质碳酸钙浆料稀释成重量含量为10%，然后将浆料送入卧式螺旋卸料离心分级机中进行分级处理，通过调整控制溢流挡板高度、转速和速差，使大颗粒出料体积流量为5%，小颗粒出料体积流量为95%，收集小颗粒浆料，大颗粒浆料返回至剥片机继...
【技术特征摘要】
1.一种超细涂布重钙浆料的制备方法，其特征在于：首先将重质碳酸钙粉制浆，将重质碳酸钙粉加入水中，并向水中加入聚丙烯酸钠分散剂，聚丙烯酸钠分散剂加入量为重质碳酸钙干粉重量的1.0%，搅拌均匀配成重质碳酸钙浆料，重质碳酸钙浆料的重量含量为50%，然后采用湿式超细剥片机对重质碳酸钙进行超细磨，制得重质碳酸钙浆料，其中小于2µm含量80～90%；将重量含量为50%的重质碳酸钙浆料稀释成重量含量为10%，然后将浆料送入卧式螺旋卸料离...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。