本发明专利技术提供了一种表面亲水性猪毛纤维，是将洗净的猪毛纤维浸润于溶解有还原剂和保护剂的水溶液中，在震摇下将溶液升温至50~85℃，在此温度下继续震摇1~5小时；冷却至室温，取出猪毛纤维，用蒸馏水冲洗，干燥，而得。该猪毛纤维在保持了原有亲油性的基础上具有了良好的亲水性，而亲水性能的有效提高使猪毛纤维的亲油性能被掩盖，从而具有水下疏油的特殊浸润性能。此类特殊浸润性材料可应用于微液滴传递技术、油水分离等应用领域。

A hydrophilic hair fiber and preparation method thereof

The present invention provides a hydrophilic surface hair fiber, is to wash the hair fiber infiltrated in the dissolved aqueous reducing agent and protective agent, shaking the solution is heated to 50~85 DEG C to jolt 1~5 hours at this temperature; cooling to room temperature, remove the hair fiber, rinsed with distilled water, drying, and. The hair fiber in the base of maintaining the original lipophilicity has good hydrophilicity, and effectively improve the hydrophilicity of the hair fiber lipophilic properties to be covered, which has special wettability and oil under water. These special wetting materials can be applied to the fields of droplet transfer technology and oil-water separation.

【技术实现步骤摘要】
一种表面亲水性猪毛纤维及其制备方法
本专利技术涉及一种具有特殊浸润性的天然高分子材料，尤其涉及一种表面亲水性猪毛纤维的制备方法，属于功能材料
及天然高分子材料领域。
技术介绍
自然界中存在许多具有特殊浸润性的生物表面，例如荷叶、蝴蝶翅膀、玫瑰花瓣、壁虎脚等，为人们设计制备新型特殊浸润材料提供了灵感。随着研究的不断深入，超疏水表面已广泛应用于生活生产等领域。然而，由于原油泄漏事故的频发和含油工业废水的排放，水体修复及水下防油污等领域的需求日益突出，开发与制备水下超疏油表面材料已成为一个亟需解决的问题。专利CN201510493493.1中制备了具有温度响应性的超亲水超疏油-油水分离膜，以织物丝网作为基材，采用浸涂或喷涂法在其上面，包裹掺杂氟烷基硅氧烷进行疏油改性的微米厚度的无机纳米粒子，同时固化构筑微纳粗糙结构。从而解决了制备工艺复杂，产率低，价格昂贵等问题。近年来，虽然有许多水下超疏油表面的报道，也开发了许多新型功能性水下超疏油表面，但是在油水分离的实际应用方面仍然存在一定距离，以及需要环境友好的分离技术。猪毛纤维富含天然角蛋白，来源丰富，价格低廉，具有良好的特殊性能，但经常被本文档来自技高网...

【技术保护点】
一种表面亲水性猪毛纤维的制备方法，是将洗净的猪毛纤维浸润于溶解有还原剂和保护剂的水溶液中，在震摇下将溶液升温至50~85℃，在此温度下继续震摇1~5小时；冷却至室温，取出猪毛纤维，用蒸馏水冲洗，干燥，得到表面亲水性猪毛纤维。

【技术特征摘要】
1.一种表面亲水性猪毛纤维的制备方法，是将洗净的猪毛纤维浸润于溶解有还原剂和保护剂的水溶液中，在震摇下将溶液升温至50~85℃，在此温度下继续震摇1~5小时；冷却至室温，取出猪毛纤维，用蒸馏水冲洗，干燥，得到表面亲水性猪毛纤维。2.如权利要求1所述表面亲水性猪毛纤维的制备方法，其特征在于：所述还原剂为亚硫酸钠、亚硫酸氢钠、硫化钠中的任意一种或两种。3.如权利要求2所述表面亲水性猪毛纤维的制备方法，其特征在于：还原剂的加入...

【专利技术属性】
技术研发人员：何玉凤，钱文珍，钱立忠，王荣民，
申请(专利权)人：西北师范大学，
类型：发明
国别省市：甘肃,62