The invention discloses a density adjustable phenolic epoxy polymer materials and a preparation method thereof, belonging to the field of solid lubricating material. The density adjustable phenolic epoxy polymer bulks, made comprises the following components by weight: 30 to 45 portions of epoxy phenolic resin, modified hollow glass beads of 20 ~ 30, 10 ~ 25 help lubricating filler, 3 to 8 portions of accelerator, curing agent 10 ~ 20, 2 ~ 5 methyl silicone oil a 3 ~ 6 active diluent. The prepared density adjustable phenolic epoxy polymer bulk density can be adjusted according to the needs, and can effectively improve the compatibility and density of similar material, and has good dimensional stability and hardness, can be widely used in heavy-duty sliding or rolling friction, is conducive to environmental protection and conservation of resources of iron and steel and polymer materials light, can reduce the mechanical load.
【技术实现步骤摘要】
一种密度可调酚醛环氧高分子块材及其制备方法
本专利技术属于固体润滑材料领域，具体涉及一种密度可调的高分子块材及其制备方法。
技术介绍
近年来随着科学技术的发展,对各种设备及零部件性能提出了越来越高的要求。而摩擦磨损是普遍存在的自然现象,世界摩擦学会的统计表明,摩擦损失了世界一次性能源的1/3以上,磨损每年造成的损失约占国民生产总值的1％。为延长使用寿命、节约材料与能源,在很多领域迫切需要解决摩擦、磨损与润滑防护问题。润滑材料有4种:气体润滑剂、流体(以油为主)、润滑脂(半固态)及固体润滑材料。液态、半固态润滑是传统的润滑方式,也是应用最为广泛的一种润滑方式,但适用的温度范围较窄,在高温作用下承载能力下降、润滑性能衰减,还会造成环境污染等问题。因此,工况恶劣的场合下,传统的润滑方法已难以满足要求。对于那些长期处于高温、高速、重载、干摩擦或边界润滑状态下的零部件,减小与控制摩擦与磨损显得尤为必要。固体自润滑材料在性能上极大地突破了传统材料的使用极限,广泛地被应用于电子、生物、航天航空等高科技领域,是润滑领域最具有发展前景的一个方向。随着现代工业等领域的飞速发展，特殊工...
【技术保护点】
一种密度可调酚醛环氧高分子块材，其特征在于，由包含以下重量份的组分制成：
【技术特征摘要】
1.一种密度可调酚醛环氧高分子块材，其特征在于，由包含以下重量份的组分制成：所述改性空心玻璃微珠是经重量比为8.5:1.5的硅烷偶联剂KH-550和异氰酸酯硅烷偶联剂在球磨机碾磨2～6小时完全水解得到的；所述改性空心玻璃微珠的种类为GS20型和GS60型空心玻璃微珠，通过改变GS20型和GS60型空心玻璃微珠的配比来调节密度可调酚醛环氧高分子块材的密度；其中：GS20的真密度在0.18～0.23g/cm3，GS60的真密度在0.58～0.64g/cm3；所述助润滑填料为滑石粉、蒙脱土、凹凸棒土和纳米碳酸钙的复配物；所述促进剂选自聚酰胺、邻苯二甲酸酐、四氢邻苯二甲酸酐、聚壬二酸酐、聚癸二酸酐、桐油酸酐、647酸酐中的一种或两种以上；所述固化剂选自T-31改性胺、593#固化剂、701#固化剂、703#固化剂、300#固化剂、650#固化剂、651#固化...
【专利技术属性】
技术研发人员：田雪梅，王圣达，田闽，乔红斌，吴胜华，古绪鹏，陈国昌，
申请(专利权)人：安徽工业大学，
类型：发明
国别省市：安徽,34