一种瓷砖美缝剂制造技术

本发明专利技术涉及一种瓷砖美缝剂，由以下组分按重量百分比混合而成：南亚128树脂50‑55％，苯扎氯胺12‑15％，壬基酚1‑3％，毕克助剂BYK‑607 2‑4％，气象二氧化硅8‑12％，稳定剂对苯二酚0.05‑0.15％，环氧活性稀释剂8‑12％，促进剂K54 0.05‑0.15％，其它助剂0.8‑1.2％，颜料6‑10％，本发明专利技术通过美缝剂配方的改善和配比的调整，使其在产品色泽度、坚硬程度、环保程度上更好，该美缝剂具有较强的粘结力，凝固后坚硬如瓷。

Ceramic tile beauty sewing agent

The invention relates to a ceramic tile seam beauty agent, which comprises the following components by weight percent: mixed into South Asia 128 resin 50 55% benzalkonium 12 15%, 1 3% grams of nonylphenol, Pichia 607 2 agent BYK 4%, 8 Meteorological silica 12%, stabilizer 0.05 0.15% hydroquinone ring. 8 oxygen reactive diluent 12%, accelerator K54 0.05 0.15%, 0.8 1.2% other additives, pigments 6 10%, the beauty of joint agents improving formula and ratio adjustment, make it better in the product color, hardness, degree of environmental protection, the United States joint agent has strong adhesive force after solidification, as hard as porcelain.

【技术实现步骤摘要】
一种瓷砖美缝剂
本专利技术属于建筑添加剂领域，尤其涉及的是一种瓷砖美缝剂。
技术介绍
瓷砖美缝剂是缝隙装饰的高档产品，适用于瓷砖，马赛克，石材等缝隙美化。他表面光洁，易于擦洗，方便清洁，防水防潮。而且其材料不含甲苯，二甲苯等有毒有害物质。目前市面上的销售的美缝剂常常存在凝固后收缩严重，不牢固，需要进行二次填缝的缺点。
技术实现思路
本专利技术的目的在于克服上述技术上的缺陷，提供一种瓷砖美缝剂。为了实现上述目的，本专利技术是通过如下的技术方案来实现：一种瓷砖美缝剂，由以下组分按重量百分比混合而成：南亚128树脂50-55％，苯扎氯胺12-15％，壬基酚1-3％，毕克助剂BYK-6072-4％，气象二氧化硅8-12％，稳定剂对苯二酚0.05-0.15％，环氧活性稀释剂8-12％，促进剂K540.05-0.15％，其它助剂0.8-1.2％，颜料6-10％。进一步的，可以由以下组分按重量百分比混合而成：南亚128树脂52％，苯扎氯胺13％，壬基酚2％，毕克助剂BYK-6073％，气象二氧化硅10％，稳定剂对苯二酚0.1％，环氧活性稀释剂10％，促进剂K541％，其它助剂0.9％，颜料8％。进一步本文档来自技高网...

【技术保护点】
一种瓷砖美缝剂，其特征在于：由以下组分按重量百分比混合而成：南亚128树脂50‑55％，苯扎氯胺12‑15％，壬基酚1‑3％，毕克助剂BYK‑607 2‑4％，气象二氧化硅8‑12％，稳定剂对苯二酚0.05‑0.15％，环氧活性稀释剂8‑12％，促进剂K54 0.05‑0.15％，其它助剂0.8‑1.2％，颜料6‑10％。

【技术特征摘要】
1.一种瓷砖美缝剂，其特征在于：由以下组分按重量百分比混合而成：南亚128树脂50-55％，苯扎氯胺12-15％，壬基酚1-3％，毕克助剂BYK-6072-4％，气象二氧化硅8-12％，稳定剂对苯二酚0.05-0.15％，环氧活性稀释剂8-12％，促进剂K540.05-0.15％，其它助剂0.8-1.2％，颜料6-10％。2.根据权利要求1所述的一种瓷砖美缝剂，其特征在于：由以下组分...