一种丝胶/甘油共混膜的制备方法及其产品和应用技术

本发明专利技术涉及一种丝胶/甘油共混膜的制备方法及其产品和应用，具体方法是将丝胶溶液与甘油混合后倒入模具中，烘干成膜，获得丝胶/甘油共混膜，利用甘油能克服丝胶的脆性和成形困难的缺点，增加丝胶膜的柔韧性，这使得丝胶膜与皮肤温和、柔软地接触，然后将丝胶/甘油共混膜通过绿色简单的方法表面原位合成纳米银，制成具有抗菌效果的纳米银/丝胶/甘油共混膜，并且具有优良的形状、稳定性和力学性能，同时具备良好生物相容性，具有重要的经济效益和社会意义。

Method for preparing sericin / glycerin blend film, product and application thereof

The invention relates to a sericin / glycerol blend membrane preparation method and its product and application, the specific method is Sericin Solution and glycerin mixture poured into a mould, dry film, obtain the sericin / glycerol blend membrane, using glycerol can overcome the brittleness of sericin and forming difficulty, increase the flexibility of the sericin film. The sericin film and skin gentle, soft contact, and then the sericin / glycerol blend membrane by in situ surface simple method of green synthesis of silver nanoparticles, made with silver nanoparticles / antibacterial effect of sericin / glycerol blend membrane, and has a shape, stability and good mechanical properties, also has good biocompatibility and has important economic and social significance.

【技术实现步骤摘要】
一种丝胶/甘油共混膜的制备方法及其产品和应用
本专利技术属于生物材料领域，具体涉及一种丝胶/甘油共混膜的制备方法，还涉及由该方法制得的产品和应用。
技术介绍
丝胶(sericin)和丝素(fibroin)是构成蚕丝蛋白的主要成分，丝胶蛋白占总蚕丝蛋白的25％-30％。丝胶具有18种氨基酸，其中大部分氨基酸具有羟基、羧基、氨基等极性基团，这些极性亲水基团赋予了丝胶良好的保湿性、吸湿性和反应活性。丝胶是一种天然的、容易获取的，且价格便宜的蛋白质资源。丝胶的高亲水性可保持伤口的湿润环境和吸收伤口渗出液，进而有助于伤口的治愈。丝胶蛋白能抗氧化、抗凝血，具有良好的生物相容性、反应活性和生物可降解性，因此丝胶蛋白被认为是理想的生物医用材料(参见文献：1、Zhang,Y.Q.,Applicationsofnaturalsilkproteinsericininbiomaterials.Biotechnologyadvances2002,20(2),91-100；2、Teramoto,H.,T.KamedaandY.Tamada."PreparationofGelFilmfromBombyxMoriSilkSericinandItsCharacterizationasaWoundDressing."BiosciBiotechnolBiochem72,no.12(2008):3189-96；3、Cao,T.T.；Zhang,Y.Q.,ProcessingandcharacterizationofsilksericinfromBombyxmorianditsapplicationinbiomaterialsandbiomedicines.Materialsscience&engineering.C,Materialsforbiologicalapplications2016,61,940-52.)。但纯丝胶固有的脆性使其成形困难，这极大地限制了丝胶在生物材料领域的应用。现有技术通过在丝胶基材料中添加PEG-DE、戊二醛、N,N0-MBAAm和DMU等化学交联剂来增加丝胶材料拉伸性能的报道。但化学交联剂的引入会带来毒性和生物相容性低的问题。纳米银因高效的抗菌效果被作为新型的抗菌剂使用。纳米银对真菌、病毒、革兰氏阳性和革兰氏阴性细菌显示出广谱的抗菌活性。纳米银已广泛用于伤口敷料、服装、食品容器、药膏和植入涂料等领域。随着纳米技术的发展，借助紫外线在材料的表面原位合成纳米银成为了一种简单有效的方法(参见文献：1、Rai,M.,A.YadavandA.Gade."SilverNanoparticlesasaNewGenerationofAntimicrobials."BiotechnolAdv27,no.1(2009):76-83；2、Ghosh,S.,R.Kaushik,K.Nagalakshmi,S.L.Hoti,G.A.Menezes,B.N.HarishandH.N.Vasan."AntimicrobialActivityofHighlyStableSilverNanoparticlesEmbeddedinAgar-AgarMatrixasaThinFilm."CarbohydrRes345,no.15(2010):2220-7；3、Lara,HumbertoH.,NildaV.Ayala-LilianadelCarmenIxtepanTurrentandCristinaRodríguezPadilla."BactericidalEffectofSilverNanoparticlesagainstMultidrug-ResistantBacteria."WorldJournalofMicrobiologyandBiotechnology26,no.4(2009):615-621；4、Zhang,K.,G.LiandY.Hu."InSituLoadingofWell-DispersedSilverNanoparticlesonNanocrystallineMagnesiumOxideforReal-TimeMonitoringofCatalyticReactionsbySurfaceEnhancedRamanSpectroscopy."Nanoscale7,no.40(2015):16952-9；5、Wang,Xumei,WenranGao,ShupingXuandWeiqingXu."LuminescentFibers:InSituSynthesisofSilverNanoclustersonSilkViaUltravioletLight-InducedReductionandTheirAntibacterialActivity."ChemicalEngineeringJournal210,(2012):585-589.)。因此，研发一种绿色无毒的，具有一定形状、稳定性和力学性能，同时具备良好生物相容性的丝胶基抗菌材料，具有重要的经济效益和社会意义。
技术实现思路
有鉴于此，本专利技术的目的之一在于提供一种丝胶/甘油共混膜的制备方法；本专利技术的目的之二在于提供由所述制备方法制得的丝胶/甘油共混膜；本专利技术的目的之三在于提供丝胶/甘油共混膜制备纳米银/丝胶/甘油共混膜的方法，本专利技术的目的之四在于提供由上述方法制得的纳米银/丝胶/甘油共混膜；本专利技术的目的之五在于提供所述纳米银/丝胶/甘油共混膜在制备抗菌材料中的应用。为实现上述专利技术目的，本专利技术提供如下技术方案：1、一种丝胶/甘油共混膜的制备方法，包括如下步骤：将丝胶溶液与甘油混合后倒入模具中，烘干成膜，获得丝胶/甘油共混膜。本专利技术中，所述丝胶溶液质量分数为1～5％，所述甘油加入量按加入后甘油对丝胶的质量比为10～50％。本专利技术中，所述烘干优选25～65℃下烘干，更优选为65℃。本专利技术中，丝胶溶液由以下方法制备：将蚕茧剪成碎片，于120℃、0.1Mpa条件下处理，然后置于-80℃的条件下冷冻8h，冷冻干燥，得到丝胶粉末，重溶制得丝胶溶液。2、由所述制备方法制得的丝胶/甘油共混膜。3、利用所述丝胶/甘油共混膜制备纳米银/丝胶/甘油共混膜的方法，将所述丝胶/甘油共混膜浸入硝酸银溶液，紫外辐射，制得纳米银/丝胶/甘油共混膜。本专利技术中，所述硝酸银浓度为20～50mM。本专利技术中，所述紫外辐射为在365nm下照射20～60min。4、由所述方法制得的纳米银/丝胶/甘油共混膜。5、所述纳米银/丝胶/甘油共混膜在制备抗菌材料中的应用。优选的，所述抗菌为抗大肠杆菌和金黄色葡萄球菌。有益效果在于：本专利技术利用丝胶蛋白和甘油的特性先制备丝胶/甘油共混膜，然后以绿色原位合成纳米银，制得的纳米银/丝胶/甘油共混膜具有以下优点：添加甘油能克服丝胶固有的脆性和成形困难的缺点，增加丝胶膜的柔韧性，适当提升丝胶膜的吸湿和保湿能力，使丝胶膜可与皮肤温和，柔软地接触；纳米银具有强大的抑菌、杀菌作用和广谱的抑菌活性，可有效抑制大肠杆菌(革兰氏阴性菌)和金黄色葡萄球菌(革兰氏阳性菌)的生长。这种纳米银/丝胶/甘油共混膜克服了丝胶的脆性问题，能有效阻挡外来细菌对创面的侵袭，且制作方便、环保、高效、价格便宜，同时共混膜中本文档来自技高网...

【技术保护点】
一种丝胶/甘油共混膜的制备方法，其特征在于，包括如下步骤：将丝胶溶液与甘油混合后倒入模具中，烘干成膜，获得丝胶/甘油共混膜。

【技术特征摘要】
1.一种丝胶/甘油共混膜的制备方法，其特征在于，包括如下步骤：将丝胶溶液与甘油混合后倒入模具中，烘干成膜，获得丝胶/甘油共混膜。2.根据权利要求1所述一种丝胶/甘油共混膜的制备方法，包括如下步骤：所述丝胶溶液质量分数为1～5％，所述甘油加入量为加入后甘油对丝胶的质量比为10～50％。3.根据权利要求1所述一种丝胶/甘油共混膜的制备方法，其特征在于，所述烘干为在25～65℃下烘干。4.由权利要求1～3任一项所述制备方法制得的丝胶/甘油共混膜。5.利用权利要求4所述丝胶/甘油共混膜制备纳米银/...

【专利技术属性】
技术研发人员：何华伟，杨梅蓉，王叶菁，蔡蕊，陶刚，赵萍，夏庆友，
申请(专利权)人：西南大学，
类型：发明
国别省市：重庆,50