一种高强度壳聚糖基水凝胶的制备方法技术
Method for preparing high strength chitosan based hydrogel
The invention discloses a preparation method of chitosan based high strength hydrogels, with chitosan as the raw material, using aqueous solution of aluminum chloride or ferric chloride chitosan solvent, aqueous solution of chitosan obtained by heating, then in aqueous solution of chitosan added in the measurement of acrylamide, acrylic acid, crosslinking agent N 'N methylenebisacrylamide and initiator by ultrasonic dissolved to obtain a homogeneous solution, followed by light induced or thermal initiation can get high strength chitosan based hydrogels. The preparation method has the advantages of simple and easy preparation, high preparation efficiency, good mechanical property of the prepared gel, high self repair and recovery, and good antibacterial property.
【技术实现步骤摘要】
一种高强度壳聚糖基水凝胶的制备方法
本专利技术属于高分子材料制备
，具体涉及一种壳聚糖基高强度水凝胶的制备方法。
技术介绍
高分子水凝胶（Hydrogel）是一类具有化学或物理的三维交联网络结构、可吸收大量水分但不溶于水的高分子或大分子聚集体。水凝胶在农用抗干旱、火灾处理、人工智能材料和生物医用材料等领域都有较大的应用前景。但传统高分子水凝胶存在网络结构不均匀和机械性能差等缺点，极大的限制了水凝胶在诸多领域的应用，尤其是在人体软骨组织如肌腱、软骨和韧带等替代的生物组织工程领域。壳聚糖是唯一的一种碱性多糖，其分子链上含有大量的活性基团——氨基和羟基，具有良好的成膜性、抗菌性、生物可降解性以及生物相容性。通过生物注射壳聚糖有助于关节软骨的痊愈，其衍生物二羧甲基壳聚糖与成骨蛋白可以促进软骨损伤的修复，此外壳聚糖可以提高间叶干细胞的粘附和增值等生物的特征，在生物组织工程领域有很大的潜在应用。但目前壳聚糖基水凝胶都存在合成工艺复杂和机械性能不佳等问题。针对壳聚糖基水凝胶较差的力学性能和强度低的问题，本专利技术提供一种简易的高性能壳聚糖基高强度水凝胶的制备方法，其先将壳...
【技术保护点】
一种壳聚糖基高强度水凝胶的制备方法，其特征在于：包括如下步骤：1）将壳聚糖加入到氯化铝或氯化铁溶液中，经加热溶解后得到壳聚糖水溶液；2）往步骤1）的壳聚糖水溶液中加入丙烯酰胺、丙烯酸、交联剂N’N‑亚甲基双丙烯酰胺和引发剂，经超声得到均匀溶液；3）将步骤2）得到的均匀溶液置于水浴加热或紫外光照下引发聚合，即可得到壳聚糖基高强度水凝胶。
【技术特征摘要】
1.一种壳聚糖基高强度水凝胶的制备方法，其特征在于：包括如下步骤：1）将壳聚糖加入到氯化铝或氯化铁溶液中，经加热溶解后得到壳聚糖水溶液；2）往步骤1）的壳聚糖水溶液中加入丙烯酰胺、丙烯酸、交联剂N’N-亚甲基双丙烯酰胺和引发剂，经超声得到均匀溶液；3）将步骤2）得到的均匀溶液置于水浴加热或紫外光照下引发聚合，即可得到壳聚糖基高强度水凝胶。2.根据权利要求1中所述的一种壳聚糖基高强度水凝胶的制备方法，其特征在于：步骤1）得到的壳聚糖水溶液中，壳聚糖浓度为2~5wt%，氯化铝或氯化铁浓度为1~3wt...
【专利技术属性】
技术研发人员：江献财，张宏翔，孟枫舒，项南平，侯琳熙，
申请(专利权)人：福州大学，
类型：发明
国别省市：福建,35