一种废旧硬质合金回收制备超细WC-Co复合粉方法技术
A waste hard alloy recovery preparation of ultrafine WC Co composite powder method
The invention belongs to the technical field of metal materials, and particularly discloses a method for preparing ultrafine WC Co composite powder waste hard alloy recovery system. It is a waste of hard alloy block oxide body is arranged on the rotary furnace in tungsten cobalt oxide loose, then mild reduction in the rotary kiln reducing atmosphere, the atmosphere in gaseous carbon reduction, carbide ultrafine WC Co composite powder. The invention of simple technology, short process, low energy consumption, high recovery rate, regeneration of the WC Co composite powder obtained by this method is of good quality. The present invention provides a method for preparing ultrafine WC Co composite powder waste hard alloy recovery system, great market value and economic value, has a good prospect in industry.
【技术实现步骤摘要】
一种废旧硬质合金回收制备超细WC-Co复合粉方法
本专利技术涉及一种废旧硬质合金回收制备复合粉的方法，尤其涉及超细WC-Co复合粉制备技术。
技术介绍
随着经济与技术的高速发展，机械制造、地质矿山、建筑、电子等行业对硬质合金和钨原料的需求量越来越大，而构成硬质合金材料主要元素钨和钴都是世界上公认的极为重要战略稀缺资源，同时原生钨的资源日益匮乏，且钴资源在我国储量极少。因此，对废旧硬质合金的再生利用越来越受到重视。由于硬质合金的硬度非常大，很难在常温下被一些无机酸碱所溶解，因此在如何回收废旧硬质合金出现了许多技术难题。目前，国内外用于回收硬质合金的方法有高温处理法、机械破碎法、锌熔法等。这些方法已显现出的主要缺点是制备的再生WC-Co粉末纯度低，粒度分布不均匀，团聚严重，回收能耗高，且对环境有危害，烧结获得的再生硬质合金材料较原生硬质合金的性能大幅度降低。因此，硬质合金工业急需研发一种工艺简便、环境友好且再生WC-Co粉末纯度高、粒度细小均匀且分布较窄，以之制备的再生硬质合金性能优良的回收新技术。对于传统的粗晶硬质合金材料，其硬度和韧性一直是一对相互制约的矛盾。近年...
【技术保护点】
一种废旧硬质合金再生WC‑Co复合粉的方法，该方法是将废旧WC‑Co硬质合金块体经氧化后得到松散的钨钴氧化物粉料，然后在还原气氛的回转炉中进行轻度还原，最后在气态碳气氛下，还原碳化制得超细WC‑Co复合粉。
【技术特征摘要】
1.一种废旧硬质合金再生WC-Co复合粉的方法，该方法是将废旧WC-Co硬质合金块体经氧化后得到松散的钨钴氧化物粉料，然后在还原气氛的回转炉中进行轻度还原，最后在气态碳气氛下，还原碳化制得超细WC-Co复合粉。2.根据权利要求1，其特征在于：所述的轻度还原气氛为H2气氛,气体流速为5~1000ml/min。3.根据权利要求1，其特征在于：所述的轻度还原温度为600~900oC，还原时间为10~180...
【专利技术属性】
技术研发人员：刘柏雄，张丽娜，杨斌，石安红，苏琪，杨高玲，
申请(专利权)人：江西理工大学，
类型：发明
国别省市：江西,36