高线免酸洗焊丝用钢的轧制方法技术
Rolling method for steel wire without pickling wire for high-speed wire
The invention discloses a wire free pickling wire rolling method for steel billet, the process is: using high speed wire production line rolling, high-speed wire rod production line consists of heating furnace, rolling zone and cooling zone; control rolling zone roughing rolling start temperature is 930 to 1000 DEG C, the temperature is 900 in rolling mill to 950 DEG C, spinning temperature is 840 to 860 DEG C; rolling zone by high-pressure gas blowing surface of the workpiece; control area of the slow speed of cold air is not higher than 1 DEG /s. This method can make the downstream users achieve wire steel wire for pickling free drawing directly, simple process, convenient operation, obvious effect, can greatly reduce the rate of broken wire drawing process, to avoid the frequent broken wires and can only speed reducing production situation and bring the staff personal safety accident.
【技术实现步骤摘要】
高线免酸洗焊丝用钢的轧制方法
本专利技术涉及一种高线焊丝钢的生产方法，尤其是一种高线免酸洗焊丝用钢的轧制方法。
技术介绍
焊丝钢的下游用户使用高线车间生产的焊丝盘条作为拔丝原料，原拔丝工艺中，焊丝钢盘条经过酸洗后能去除盘条表面大部分氧化铁皮粉末，对拔丝过程无影响。目前，焊丝钢拔丝厂迫于当地政府环保、成本的压力，纷纷采用取消初拔前的酸洗工艺进行拔丝。由于其生产工艺变化，由原酸洗改为免酸洗，经过机械除鳞再进行初拔，导致焊丝盘条在拉拔过程中，氧化铁皮不易剥落，极易堵塞拔丝眼膜，频繁断线；焊丝钢拔丝厂只能降速生产（从每分钟850米降至600米），极大地影响到焊丝钢用户的产量。综上所述，焊丝钢下游用户的生产工艺变化，无论是从作业速度还是从作业质量上来讲，都急需焊丝钢盘条原料生产企业打破目前的固有生产模式，探索一种工艺简单、便于操作、效果明显的免酸洗焊丝用钢的新生产方法。
技术实现思路
本专利技术要解决的技术问题是提供一种工艺简单的高线免酸洗焊丝用钢的轧制方法。为解决上述技术问题，本专利技术所采取的技术方案是：铸坯采用高速线材生产线进行轧制，高速线材生产线包括加热炉、轧制区和风冷...
【技术保护点】
一种高线免酸洗焊丝用钢的轧制方法，其特征在于：铸坯采用高速线材生产线进行轧制，高速线材生产线包括加热炉、轧制区和风冷区；控制轧制区粗轧的开轧温度为930～1000℃，进精轧机温度为900～950℃，吐丝温度为840～860℃；轧制区的机架间采用高压气体吹扫轧件表面；控制风冷区的缓冷冷速≤1℃/s。
【技术特征摘要】
1.一种高线免酸洗焊丝用钢的轧制方法，其特征在于：铸坯采用高速线材生产线进行轧制，高速线材生产线包括加热炉、轧制区和风冷区；控制轧制区粗轧的开轧温度为930～1000℃，进精轧机温度为900～950℃，吐丝温度为840～860℃；轧制区的机架间采用高压气体吹扫...