The invention discloses a method for preparing hydroxyapatite biomaterial, which includes the following steps: hydroxyapatite slurry water bath heating, filtering and collecting residue, drying, grinding and sieving, modified nano hydroxyapatite powder; dispersing the inorganic nano particles injected into a twin-screw extruder, with polylactic acid particles blending, heating until all the water has evaporated, the mixture of A; the nano hydroxyapatite powder mixture of A and mixed income, acrylic additives added blending perfluoroalkyl, mixture B; according to the proportion of the chitosan acetic acid solution mixed with 2% B mixture mixing, making the mixture B completely dispersed set the chitosan acetic acid solution, the mixture of C; from a mixture of C, drop by drop added to the NaOH solution, generating gel beads, curing, separation, washing to neutral, dry Dryness leads to dryness. The biological material obtained by the invention has the advantages of uniform composition and organization, low elastic modulus and good biological activity.
【技术实现步骤摘要】
一种羟基磷灰石复合生物材料的制备方法
本专利技术涉及生物材料制备领域,具体涉及一种羟基磷灰石复合生物材料的制备方法。
技术介绍
羟基磷灰石是天然骨的主要无机成分,以HA为基础的陶瓷材料,因其组成成分、结构性质与人体骨无机质相似,并具有良好的生物相容性、骨引导作用,可与自然骨形成生物性的键合,而成为研究的热点。但是该类材料由于脆性大,在医学上主要用于非承重部位;为了提高其韧性,羟基磷灰石/聚合物复合材料被广泛研究和应用。采用纳米羟基磷灰石晶体(n-HA)与聚合物复合,可望提高其在聚合物中的含量和在聚合物中的均匀分散性,从而提高复和材料的韧性。聚乳酸是一种具有优良的生物相容性和可生物降解性的合成高分子材料。这种线型热塑性生物可降解脂肪族聚酯是以玉米、小麦、木薯等一些植物中提取的淀粉为最初原料,经过酶分解得到葡萄糖,再经过乳酸菌发酵后变成乳酸,然后经过化学合成得到高纯度聚乳酸。通过将聚合物与复合材料聚乳酸相结合,提高其复合材料的韧性,但是一般这类物质与身体结合程度较低,身体容易形成排斥反应,所以需要一种韧性较强的、与人体结合度较高的骨材料很有必要。
技术实现思路
为解决上述 ...
【技术保护点】
一种羟基磷灰石复合生物材料的制备方法,其特征在于,包括如下步骤:S1、将硬脂酸通过超声波振荡设备分散于无水乙醇中形成硬脂酸分散液,按质量比1∶5,将羟基磷石灰与硬脂酸分散溶液搅拌混合,制备得羟基磷石灰浆料,随后将其置于60~70℃水浴加热0.5~1.5h;S2、待加热完成后,对其抽滤并收集滤渣,将其置于80~90℃烘箱中干燥30~38h,随后将其置于10~15MPa下进行碾磨并过筛,得100~120目的改性纳米羟基磷石灰粉末;S3、将无机纳米粒子通过超声波振荡设备分散于纯净水中形成无机纳米粒子分散液;S4、将步骤S3所得无机纳米粒子分散液通过液体喂料泵注入双螺杆挤出机,与聚 ...
【技术特征摘要】
1.一种羟基磷灰石复合生物材料的制备方法,其特征在于,包括如下步骤:S1、将硬脂酸通过超声波振荡设备分散于无水乙醇中形成硬脂酸分散液,按质量比1∶5,将羟基磷石灰与硬脂酸分散溶液搅拌混合,制备得羟基磷石灰浆料,随后将其置于60~70℃水浴加热0.5~1.5h;S2、待加热完成后,对其抽滤并收集滤渣,将其置于80~90℃烘箱中干燥30~38h,随后将其置于10~15MPa下进行碾磨并过筛,得100~120目的改性纳米羟基磷石灰粉末;S3、将无机纳米粒子通过超声波振荡设备分散于纯净水中形成无机纳米粒子分散液;S4、将步骤S3所得无机纳米粒子分散液通过液体喂料泵注入双螺杆挤出机,与聚乳酸颗粒共混,加热至水全部蒸发,得混合物A;S5、将步骤S2所得的改性纳米羟基磷灰石粉末与混合物A混合后,加入适量全氟烷基的丙烯酸系添加剂通过双螺杆挤出机共混造粒,螺杆挤出机转速为600~900rpm,压力为2~3MPa,经过熔融挤出,造粒,得混合物B,备用;S6、按重量份计,配制100份2%的醋酸溶液,然后在醋酸溶液中加入2份壳聚糖粉末,搅拌24h,至溶液透明均匀,没有气泡,配制成质量百分比为2%的壳聚糖醋酸溶液;S7、按固液...