提供一种聚缩醛共聚物的制造方法，其能有效地抑制聚合反应器内部的结垢的产生从而可以实现长期稳定运转和高聚合收率化，并且即使用少量的聚合催化剂也能够保持聚合收率。一种聚缩醛共聚物的制造方法，其中，所述制造方法包括将三氧杂环己烷、环状醚和/或环状缩甲醛、聚合催化剂、低分子量缩醛化合物和有机溶剂供给到聚合反应器中而进行聚合的工序，而且将具有环状结构的化合物和具有直链结构的化合物并用作为所述有机溶剂。

Process for producing polyacetal copolymer

To provide a method for producing polyacetal copolymer, which can effectively suppress the polymer fouling inside the reactor which can realize long-term stable operation and high yield of polymerization is used, and a small amount of polymerization catalyst can maintain the polymerization yield. One method of manufacturing polyacetal copolymer, the manufacturing method comprises three oxygen heterocyclic hexane, cyclic ether and / or cyclic acetal, catalyst, low molecular weight acetal compounds and organic solvent is supplied to the polymerization reactor polymerization and polymerization process, and a compound having a ring structure and a compound having straight chain structure and used as the organic solvent.

【技术实现步骤摘要】
聚缩醛共聚物的制造方法
本专利技术涉及聚缩醛共聚物的制造方法。
技术介绍
聚缩醛共聚物为刚性、韧性等机械强度、滑动性和蠕变性等优异的树脂，在以汽车部件、电气/电子设备和各种机构部件为中心的广泛范围内得到使用。使用所述聚缩醛共聚物的汽车部件、电气/电子设备和各种机构部件多为重要的部件，其品质稳定化、即通过成型得到的部件的品质偏差小是重要的。为了实现所述的品质稳定化，制造聚缩醛共聚物时的长期稳定运转是重要的。以往以来，在制造聚缩醛共聚物时，如下情况成为问题：在聚合反应器的内部产生结垢阻碍长期稳定运转，另外，还引起聚合收率的降低。作为减少这样的结垢的产生的技术之一，可以列举减少在制造聚缩醛共聚物时使用的聚合催化剂。作为能够减少在制造聚缩醛共聚物时使用的聚合催化剂的技术，公开了例如预先将环状醚和/或环状缩甲醛、低分子量缩醛化合物和聚合催化剂混合而得到预混合物、并将该预混合物添加供给到三氧杂环己烷中而进行聚合的技术(例如，参见专利文献1)；或者预先将环状醚和/或环状缩甲醛、聚合催化剂和有机溶剂混合而得到预混合物、并使该预混合物与三氧杂环己烷接触而进行聚合的技术(例如，参见专利文献2)。它们均为本文档来自技高网...

【技术保护点】
一种聚缩醛共聚物的制造方法，其中，所述制造方法包括将三氧杂环己烷、环状醚和/或环状缩甲醛、聚合催化剂、低分子量缩醛化合物和有机溶剂供给到聚合反应器中而进行聚合的工序，而且将具有环状结构的化合物和具有直链结构的化合物并用作为所述有机溶剂。

【技术特征摘要】
2015.10.28 JP 2015-2121851.一种聚缩醛共聚物的制造方法，其中，所述制造方法包括将三氧杂环己烷、环状醚和/或环状缩甲醛、聚合催化剂、低分子量缩醛化合物和有机溶剂供给到聚合反应器中而进行聚合的工序，而且将具有环状结构的化合物和具有直链结构的化合物并用作为所述有机溶剂。2.如权利要求1所述的聚缩醛共聚物的制造方法，其中，所述有机溶剂为脂肪族烃。3.如权利要求1或2所...