具有适宜孔隙率和力学强度的HA多孔陶瓷的制备方法及其产品技术
Method for preparing HA porous ceramic with suitable porosity and mechanical strength and products thereof
The invention relates to a porous HA ceramics with suitable porosity and mechanical strength of the preparation method and its products, the specific method for rod shaped HA particles (R HA) and spherical HA particles (s HA) mixed after soaking in distilled water, stirring to form uniform mixing of polyacrylamide, ceramic slurry then, forming, made of ceramic precursor, then sintered HA porous ceramics, the effect of R HA and s HA mixed sintering porosity and mechanical strength of ceramics, porous HA ceramics prepared suitable porosity and mechanical strength, can be used as bone tissue repair and regeneration of stent.
【技术实现步骤摘要】
具有适宜孔隙率和力学强度的HA多孔陶瓷的制备方法及其产品
本专利技术属于生物材料领域，涉及一种具有适宜孔隙率和力学强度的HA多孔陶瓷的制备方法，还涉及制得的HA多孔陶瓷。
技术介绍
羟基磷灰石(HA)生物陶瓷支架常被用作促进骨组织修复和再生的桥连，因HA与自然骨组织矿物相具有相同的组成，不仅安全、无毒还兼具生物活性和骨传导性。HA生物陶瓷支架中含有适当尺寸的孔隙，并占有一定的体积分数，对陶瓷和组织之间的相互作用有重要作用，即新生骨可以从HA与原骨结合处沿着HA陶瓷表面并向陶瓷内部攀附生长，与周围骨组织形成良好的骨性结合，促进骨的再生和重建。但正是由于HA生物陶瓷的多孔性，导致其支架的本体力学强度不足，限制了它在承重部位骨生长重建中的应用。鉴于此，大量研究试图通过不同的制备方法和致孔剂来控制陶瓷孔隙结构，包括孔隙率，孔径，孔的形状和分布等，以此来获得力学强度与功能兼备的HA多孔陶瓷，取得了一定的效果。然而，HA多孔陶瓷的力学性能除受孔结构影响以外，还与HA颗粒的烧结性能密切相关。颗粒间良好的烧结与融合有利于形成强度更高的支架。但是，不同HA颗粒形状能调控HA多孔陶瓷...
【技术保护点】
具有适宜孔隙率和力学强度的HA多孔陶瓷的制备方法，其特征在于，包括如下步骤：将棒形HA颗粒与球形HA颗粒按质量比为80:20～20:80混合后浸泡于蒸馏水中，搅拌下加入聚丙烯酰胺，搅拌至形成均匀的陶瓷泥浆，然后成型，制成陶瓷前体，再烧结得HA多孔陶瓷。
【技术特征摘要】
1.具有适宜孔隙率和力学强度的HA多孔陶瓷的制备方法，其特征在于，包括如下步骤：将棒形HA颗粒与球形HA颗粒按质量比为80:20～20:80混合后浸泡于蒸馏水中，搅拌下加入聚丙烯酰胺，搅拌至形成均匀的陶瓷泥浆，然后成型，制成陶瓷前体，再烧结得HA多孔陶瓷。2.根据权利要求1所述具有适宜孔隙率和力学强度的HA多孔陶瓷的制备方法，其特征在于：所述棒形HA颗粒与球形HA颗粒按质量比为60:40～40:60混合。3.根据权利要求1所述具有适宜孔隙率和力学强度的HA多孔陶瓷制备方法，其特征在于：所述聚丙烯酰胺的加入量按棒形HA颗粒与球形HA颗粒的混合物：聚丙烯酰胺的质量比为1：3～10：1。4.根据权利要求3所述具有适宜孔隙率和力学强度的HA多孔陶瓷的制备方法，其特征在于：所述聚丙烯酰胺的加入量按棒形HA颗粒与球形HA颗粒的混合物：聚丙烯酰胺的质量比为1：1～5：1。5.根据...
【专利技术属性】
技术研发人员：罗彦凤，吴进川，王远亮，
申请(专利权)人：重庆大学，
类型：发明
国别省市：重庆,50