The invention discloses a liquid rust proof gloves and a preparation method thereof, which is composed of casein, latex, glycerin, triethanolamine, ethanol, distilled water, dibutyl phthalate; during preparation of casein will be added to the reactor with water, distilled water adding amount of 90%, advance water bath heating to 70 DEG C, stirring 1 ~ 1.5h, in the process of mixing residual distilled water was added, the casein fully expanded and stirring; adding triethanolamine, making the materials in the reaction kettle as glue liquid; then slowly adding glycerin and dibutyl phthalate and stirring continuously; the mixture of ethanol and finally adding emulsion solution, stirring and mixing evenly, the formula of the invention; simple and convenient preparation, use quickly, creating a great convenience for the processing of mechanical parts, but also for regular contact with The solvent population has brought about an effective barrier that contributes to people's health.
【技术实现步骤摘要】
一种液体防锈手套及其制备方法
本专利技术属于机械加工
,特别是一种液体防锈手套及其制备方法。
技术介绍
在机械零件加工过程中,操作工不可避免的要接触到工件的表面,为了避免手上的汗液接触到工件引起工件生锈,常常需要乳胶佩戴手套,然而乳胶手套具有不透气的特性,长时间使用,工人手指很容易发生肿胀,进而容易引发生产事故,此外,成品工件检验、精密仪器的装配等工作也需要工作人员戴手套隔离手汗,而使操作人员身体感觉不舒服;还有在一些特殊行业中,操作工需要经常接触汽油、煤油、香蕉水等有机溶剂,给人体带来伤害,而戴手套操作又存在极大的不方便,因此,研发一种能使操作工在从事上述工作时能够方便涂抹,而又能有效隔绝手上产生的汗液与工件之间的接触的液体手套十分必要。
技术实现思路
本专利技术的目的就是要解决目前再机械零件加工或者一些特殊行业中,因为怕工件与手在无乳胶手套隔绝时容易将汗液带到工件上,引起工件产生锈蚀的问题,提供一种液体防锈手套及其制备方法。本专利技术的一种液体防锈手套,由下述重量份原料组成:干酪素5~15乳胶0.5~2甘油3~8三乙醇胺0.5~2乙醇20~30蒸馏水20~30邻苯二甲酸二丁酯3~8。本专利技术的一种液体防锈手套的制备方法,由下述步骤组成:(1)将干酪素加入带水浴的反应釜内,加入配方用量90%的蒸馏水,水浴事先加热至70℃;(2)将反应釜内的物料在70℃下保温搅拌1~1.5h,在搅拌过程中将余量蒸馏水继续加入,使干酪素充分膨胀;(3)向反应釜内加入三乙醇胺并充分搅拌,使反应釜内的物料成为胶液状;(4)向反应釜内缓慢加入甘油和邻苯二甲酸二丁酯并不断搅拌; ...
【技术保护点】
一种液体防锈手套,其特征在于由下述重量份原料组成:干酪素 5~15 乳胶 0.5~2甘油 3~8 三乙醇胺 0.5~2乙醇 20~30 蒸馏水 20~30邻苯二甲酸二丁酯 3~8。
【技术特征摘要】
1.一种液体防锈手套,其特征在于由下述重量份原料组成:干酪素5~15乳胶0.5~2甘油3~8三乙醇胺0.5~2乙醇20~30蒸馏水20~30邻苯二甲酸二丁酯3~8。2.如权利要求1所述的一种液体防锈手套的制备方法,其特征在于由下述步骤组成:(1)将干酪素加入带水浴的反应釜内,加入配方用量90%的蒸馏水,水浴事先加...