一种铝铜合金接地材料焊接用焊丝及其制备方法技术

本发明专利技术公开了一种铝铜合金接地材料焊接用焊丝及其制备方法，该焊丝的质量百分比组成为：硅1%～3%，铜1%～3%，铁≤0.3%，锆0.001‑0.05%，稀土0.001%～0.5%，余量为铝。本发明专利技术的铝铜合金接地材料用焊丝可实现铝铜合金接地材料的焊接，焊缝区组织细密，成分与母材相近，电位差小，具有较好的耐土壤腐蚀性能。

An aluminum alloy grounding material welding wire and preparation method

The invention discloses an aluminum alloy grounding material welding wire and preparation method, the quality of the wire is composed of: the percentage of silicon 1% ~ 3%, 1% ~ 3% copper, iron is less than or equal to 0.3%, 0.001 zirconium 0.05%, rare earth 0.001% ~ 0.5%, the other is aluminum. The welding of Al Cu alloy of the invention can realize the grounding wire materials of Al Cu alloy grounding material, weld zone is very fine, and the parent material of similar composition, the potential difference is small, has good resistance to soil corrosion.

【技术实现步骤摘要】
一种铝铜合金接地材料焊接用焊丝及其制备方法
本专利技术涉及一种焊接材料，特别是用于铝铜合金接地材料焊接的铝合金焊丝及其制备方法。
技术介绍
变电站接地网是维护电力系统安全可靠运行、保证人员和设备安全的关键构件。接地网用铝铜合金材料是目前较为理想的接地网材料，其具有以下优点：能够承受强大的接地电流；对于变电站所处地区的土壤环境具有良好的耐腐蚀性，满足对接地网使用寿命的要求等。GB50169-2006《电器装置安装工程接地装置施工及验收规范》中3.41规定接地体(线)的连接应采用焊接，焊接必须牢固无虚焊。由于铝合金材料本身的物理特性与其他金属不同，例如比热容、电导率、热导率比钢大，焊接时的热输入将向母材迅速流失，需采用高度集中的热源，使得铝铜合金材料的焊接相比于其他合金材料(比如钢)具有很大的焊接难度。针对铝铜合金接地材料的焊接，采用的是常规的Al-Si系焊丝和Al-Cu系焊丝，其中，Al-Si系焊丝是指ER4047、ER4043，Al-Cu系焊丝是指ER2319、ER4145，采用这些焊丝对铝铜合金接地材料进行焊接，尽管接头的力学性能均能满足要求，但由于焊丝的成分与母材不匹配，使得接头本文档来自技高网...

【技术保护点】
一种铝铜合金接地材料焊接用焊丝，其特征是，其质量百分比组成为：硅1%～3%，铜1%～3%，铁≤0.3%，锆0.001‑0.05%，稀土0.001%～0.5%，余量为铝。

【技术特征摘要】
1.一种铝铜合金接地材料焊接用焊丝，其特征是，其质量百分比组成为：硅1%～3%，铜1%～3%，铁≤0.3%，锆0.001-0.05%，稀土0.001%～0.5%，余量为铝。2.一种铝铜合金接地材料焊接用焊丝，其特征是，其质量百分比组成为：硅1%～1.5%，铜2.5%～3%，铁0.1-0.3%，锆0.002-0.003%，稀土0.05%～0.08%，余量为铝。3.一种铝铜合金接地材料焊接用焊丝，其特征是，其质量百分比组成为：硅1.5%，铜2.5%，铁0.3%，锆0.002%，稀土0.08%，余量为铝。4.如权利要求1~3中任一项所述的焊丝，其特征是：所述稀土为镧、铈、钕、钇中的至少一种。5.权利要求1~4中任一项所述的铝铜合金接地材料焊接用焊丝的制备方法，其特征是，包括以下步骤：将铝锭加热熔化，按比例加入其它各原材料的母合金，当原料在熔池里充分熔化，进行扒渣搅拌，然后取样检测调整成分，精炼，再浇注成棒状铝合金铸锭；采...

【专利技术属性】
技术研发人员：闫风洁，李辛庚，岳增武，王晓明，樊志彬，郭凯，傅敏，孙伟，翟季青，刘延华，
申请(专利权)人：国网山东省电力公司电力科学研究院，国家电网公司，
类型：发明
国别省市：山东,37