The present invention provides a method for preparing nano aluminum polyester composite conductive fabric, relates to the technical field of textile finishing, the method comprises the following steps: (1) the phenol soluble in ethanol; (2) the dispersion of nano aluminum powder to ethanol / mixed phenol, white dispersion solution under ultrasound; (3) the polyester fabric into the dye and heated to 40~60 degrees C oscillation, heat preservation duration 5~30min; (4) were finally washed with ethanol for several times, after taking out 80 degrees C drying, can obtain nano aluminum conductive polyester fabric. The preparation technique has the advantages of simple process, no high temperature condition and complex reaction equipment, and good conductive property of the conductive fabric.
【技术实现步骤摘要】
纳米铝粉复合涤纶导电织物的制备方法
本专利技术涉及纺织品整理
,具体涉及一种纳米铝粉复合涤纶导电织物的制备方法。
技术介绍
导电织物具有导电、抗静电和抗电磁辐射功能,能够制备传感器、智能服装和可折叠电池等高科技产品,因此在传感器、化学、生物、医学和航空航天等多个领域都有重要的作用。以涤纶为基底的复合导电织物由于质量轻,原料易得,价格便宜,稳定性好,电导率可调等特点,是最有前途的导电织物之一。
技术实现思路
本专利技术所要解决的问题是提供一种制备工艺简单,导电性好的纳米铝粉复合涤纶导电织物的制备方法,本专利技术采取如下技术方案。一种纳米铝粉复合涤纶导电织物的制备方法,包括如下步骤:(1)将苯酚溶于乙醇中;(2)将纳米铝粉分散于乙醇/苯酚混合溶液中,超声下得到白色分散溶液;(3)将涤纶织物投入到上述溶液中,振荡加热至30~60ºC,保温持续5~30min;(4)分别用乙醇洗涤数次,取出后80ºC下烘干,即可获得纳米铝粉导电涤纶织物。进一步的,所述的乙醇/苯酚混合溶液的乙醇与苯酚的质量比为1:0.1~3。进一步的,所述的纳米铝粉与乙醇/苯酚混合溶液的质量比为1:100~1000。本专利技术的有益效果在于,纳米铝粉复合涤纶导电织物的制备方法简单,不需要高温条件和复杂的反应设备;制备的导电织物的导电性好。具体实施方式下文将结合具体实施例详细描述本专利技术。应当注意的是,下述实施例中描述的技术特征或者技术特征的组合不应当被认为是孤立的,它们可以被相互组合从而达到更好的技术效果。实施例1纳米铝粉复合涤纶导电织物的制备方法详细步骤如下:(1)将20g苯酚溶于180g乙醇 ...
【技术保护点】
一种纳米铝粉复合涤纶导电织物的制备方法,其特征在于,包括如下步骤:(1)将苯酚溶于乙醇中;(2)将纳米铝粉分散于乙醇/苯酚混合溶液中,超声下得到白色分散溶液;(3)将涤纶织物投入到上述溶液中,振荡加热至40~60ºC,保温持续5~30min;(4)分别用乙醇洗涤数次,取出后80ºC下烘干,即可获得纳米铝粉导电涤纶织物。
【技术特征摘要】
1.一种纳米铝粉复合涤纶导电织物的制备方法,其特征在于,包括如下步骤:(1)将苯酚溶于乙醇中;(2)将纳米铝粉分散于乙醇/苯酚混合溶液中,超声下得到白色分散溶液;(3)将涤纶织物投入到上述溶液中,振荡加热至40~60ºC,保温持续5~30min;(4)分别用乙醇洗涤数次,取出后80º...
【专利技术属性】
技术研发人员:卢明,赵振云,周菁,刘一萍,胡睿敏,蒲青霞,董倩,刘欣,
申请(专利权)人:西南大学,
类型:发明
国别省市:重庆,50