The invention discloses an anti exposure PVC hard pipe, including: PVC resin, two lead phosphite, three base lead sulfate, lead stearate, calcium stearate, carbon black, the weight of each component is PVC resin 100, two base lead phosphite 0.7~1, three base lead sulfate, stearic 1~2 lead acid 0.2~0.8, stearic acid 0.6~1, black 1~2, its preparation method is as follows: the raw material components, through kneading, extrusion, cooling, cutting, after the test was finished. The PVC hard tube prepared by the invention has good heat resistance and can be used in field laying and direct sunlight environment.
【技术实现步骤摘要】
一种防暴晒PVC硬管及其制备方法
本专利技术涉及一种防暴晒PVC硬管及其制备方法,应用于PVC加工
技术介绍
随着科学的进步,PVC管材得到快速的发展,将逐步代替传统管材,但由于纯的PVC树脂属于一类强极性聚合物,其分子间的作用力较大,导致了PVC软化和熔融温度较高,同时PVC分子内含有的取代氯基容易导致PVC树脂脱氯化氢反应,使得PVC对热极不稳定,温度身高会大大促进PVC脱HCL反应,从而导致了PVC降解,PVC硬管常用于供水设备中,但我国版图辽阔,许多水管安装在野外,没有防晒措施,常规的PVC硬管不能够满足于野外作业。
技术实现思路
为解决上述的问题,本专利技术公开了一种防暴晒PVC硬管及其制备方法,制得的PVC硬管耐热性好,能够适用于野外铺设。本专利技术公布了一种防暴晒PVC硬管,包括:PVC树脂、二盐基亚磷酸铅、三盐基硫酸铅、硬脂酸铅、硬脂酸钙、炭黑,各组分的重量份数为PVC树脂100份、二盐基亚磷酸铅0.7~1份、三盐基硫酸铅1~2份、硬脂酸铅0.2~0.8份、硬脂酸0.6~1份、炭黑1~2份。上述一种防暴晒PVC硬管,其制备方法为,取各组分的上述原料,经捏合、挤出成型、冷却定形、切割、检验后得成品。在上述配方中,各组元的作用如下:二盐基亚磷酸铅、三盐基硫酸铅:协同使用,具有热稳定性能优良、稳定效果持久的优点;硬脂酸铅:作为热稳定性及润滑剂,同时具备光稳定作用;硬脂酸:具有良好的润滑性以及光、热稳定性;炭黑:补强、耐磨以及作为色素使用。采用本技术方案,本专利技术的有益效果是:所制得的硬管能够置于阳光下暴晒,热稳定性能好,使用寿命长。具体实 ...
【技术保护点】
一种防暴晒PVC硬管,其特征在于,包括:PVC树脂、二盐基亚磷酸铅、三盐基硫酸铅、硬脂酸铅、硬脂酸钙、炭黑,各组分的重量份数为PVC树脂100份、二盐基亚磷酸铅0.7~1份、三盐基硫酸铅1~2份、硬脂酸铅0.2~0.8份、硬脂酸0.6~1份、炭黑1~2份。
【技术特征摘要】
1.一种防暴晒PVC硬管,其特征在于,包括:PVC树脂、二盐基亚磷酸铅、三盐基硫酸铅、硬脂酸铅、硬脂酸钙、炭黑,各组分的重量份数为PVC树脂100份、二盐基亚磷酸铅0.7~1份、三盐基硫酸铅1~2份、硬脂酸铅0.2~0.8份、硬脂酸0.6~1份、炭黑1~2份。2.如权利要求1中所述的战役中防暴晒PVC硬管,其特征在于,其制备方法为:取各组分的上述原料,经捏合、挤出成型、冷却定形、切割、检验后得成品。3.根据权利要求1所述的一种防暴晒PVC硬管,其特征在于,包括...
【专利技术属性】
技术研发人员:王新志,
申请(专利权)人:安徽圣源橡塑科技有限公司,
类型:发明
国别省市:安徽,34