The invention discloses inorganic insulating coating material and a preparation method of kiln wall, made of powder and water according to the weight of 1:1 ~ 1.6 mixing; which includes 50 perlite: powder 60, carboxymethyl cellulose 30 35 copies, 65 copies of the 32 filling material. Filling material by glass beads of 5 10 copies, 10 copies, 5 sepiolite cenosphere 10 20, Russia velvet 10 20, 2 5 parts of clay. The carboxymethyl cellulose is first dissolved in water and then mixed with other powder and water. The inorganic thermal insulation coating material for the exterior wall of the kiln has good thermal shock resistance, small corrosion resistance to the external wall material of the furnace and stable performance.
【技术实现步骤摘要】
窑炉外墙用无机保温涂层材料及其制备方法
本专利技术涉及无机材料
,特别涉及一种窑炉外墙用无机保温涂层材料,同时还涉及该窑炉外墙用无机保温涂层材料的制备方法。
技术介绍
窑体的耐火材料,在窑炉升温加热的工作过程中,要吸收和逸散大量窑内燃料燃烧所产生的热量,成为窑炉能耗的主要原因之一。陶瓷行业使用的窑炉,其耐火材料大部分采用A12O3-SiO2体系的无机材料,如果在窑炉内衬涂覆具有高辐射系数的涂层材料,将改善A12O3-SiO2体系耐火材料的辐射性能,燃料燃烧热量由于窑炉内衬辐射性能的提高,更多的作用于被加热的产品上,外墙保温减少热量散失这将减少产品烧成的热量消耗,降低燃料的消耗,达到节能的目的。因此,但现有窑炉使用中,涂层容易龟裂脱落,影响使用效果和使用寿命。因此根据基体材料选择合适的涂层填充材料和辐射材料,是提高涂层的抗热震性能、改善与窑炉内外材料结合的重要方向之一。
技术实现思路
本专利技术的目的在于克服上述缺点而提供的一种抗热震性能优良、对炉外墙材料腐蚀性小、性能稳定的窑炉外墙用无机保温涂层材料。本专利技术的另一目的在于提供该窑炉外墙用无机保温涂层材料的制备方法。本专利技术的一种窑炉外墙用无机保温涂层材料,由粉剂和水按重量1:1~1.6混合搅拌制成;其中:粉剂包括保温料50-60份、粘结料30-35份、填充料32-65份。上述的一种窑炉外墙用无机保温涂层材料,其中:填充料由玻化微珠5-10份,海泡石5-10份、漂珠10-20份,俄罗斯绒10-20份,粘土2-5份组成。上述的一种窑炉外墙用无机保温涂层材料,其中:保温料为珍珠岩。上述的一种窑炉外墙用无机 ...
【技术保护点】
一种窑炉外墙用无机保温涂层材料,由粉剂和水按重量1:1~1.6混合搅拌制成;其中:粉剂包括保温料50‑60份、粘结料30‑35份、填充料32‑65份。
【技术特征摘要】
1.一种窑炉外墙用无机保温涂层材料,由粉剂和水按重量1:1~1.6混合搅拌制成;其中:粉剂包括保温料50-60份、粘结料30-35份、填充料32-65份。2.如权利要求1所述的一种窑炉外墙用无机保温涂层材料,其中:填充料由玻化微珠5-10份,海泡石5-10份、漂珠10-20份,俄罗斯绒1...