The utility model relates to a two time silicon mullite brick coating material, belonging to the technical field of refractory materials for cement kiln waste heat power generation. The weight percentage composition: each component weight percentage: two silicon particle size less than 3mm Mo brick 45 ~ 55%, 2 ~ 6% silica fume, aluminate cement 8 ~ 15%, 5 ~ 10% clay, high alumina powder from 10 to 15%, 180 to 3 ~ 8% silica powder, alumina powder from 8 to 15%, the other the additive is added. The utility model has the advantages that the waste material is used for the two time, and the products made of the utility model have the advantages of high strength, good abrasion resistance, easy construction, etc..
【技术实现步骤摘要】
一种二次硅莫砖涂抹料
本专利技术属于水泥窑余热发电用耐火材料
，特别提供了一种二次硅莫砖涂抹料。尤其涉及一种以二次硅莫砖为骨料的水泥窑余热发电用高强耐磨涂抹料。
技术介绍
目前我国年消耗耐火材料约1000万吨，废旧耐火材料达到400万吨，为节约工业产品的成本，废旧耐火材料的循环再利用是一条可行之路，不仅可大幅度降低耐火材料的制备成本，还能带来显著的经济与社会效益。目前，有关的试验研究结果显示：采用高比例的二次耐火材料可以制成优质的耐火砖、浇注料、捣打料等产品，而且产品性能可接近或高于原产品的水平，因此，在耐火原材料市场价格不断攀升，耐火制成品市场价格却受用户成本需求而不断下降，充分利用二次耐材，具有非常现实的意义。在不定形耐火材料中，水泥窑是重要的应用方向。水泥窑余热发电的管道设备中的烟气中带着磨损性较强的熟料微粒，该微粒具有粉尘粒径粗、磨损性大等特点，会严重磨损锅炉，降低锅炉的使用寿命。且余热发电设备中的风管变径多，弯头多，风速快，磨损严重。为满足余热发电发展需要，须加快耐火材料的技术进步，用于余热发电的耐火材料必须有极高的耐磨性，良好的耐碱性、韧性、抗热震性能，还有良好的施工性能。
技术实现思路
本专利技术的目的在于提供一种二次硅莫砖涂抹料，解决了废旧硅莫砖循环再利用以及耐火材料耐磨性差的问题。产品具有优良的耐磨性，强度高，施工性能好，可显著提高锅炉及连接锅炉的风管的使用寿命。一种二次硅莫砖涂抹料，各成分质量百分比为：粒度≤3mm的二次硅莫砖45～55％，硅灰2～6％，铝酸盐水泥8～15％，粘土5～10％，高铝细粉10～15％，180目的硅砖粉3～8...
【技术保护点】
一种二次硅莫砖涂抹料，其特征在于，各成分质量百分比为：粒度≤3mm的二次硅莫砖45～55％，硅灰2～6％，铝酸盐水泥8～15％，粘土5～10％，高铝细粉10～15％，180目的硅砖粉3～8％，氧化铝粉8～15％；另加入外加剂，占上述各物质总和质量的0.02～0.23％。
【技术特征摘要】
1.一种二次硅莫砖涂抹料，其特征在于，各成分质量百分比为：粒度≤3mm的二次硅莫砖45～55％，硅灰2～6％，铝酸盐水泥8～15％，粘土5～10％，高铝细粉10～15％，180目的硅砖粉3～8％，氧化铝粉8～15％；另加入外加剂，占上述各物质总和质量的0.02～0.23％...
【专利技术属性】
技术研发人员：夏银凤，冯立新，王国飞，
申请(专利权)人：通达耐火技术股份有限公司，北京通达绿色高温新材料工程研究中心有限公司，
类型：发明
国别省市：北京,11