The invention discloses a method for the field of municipal engineering and non slip rubber material with corrosion resistance and wear resistance, which is composed of styrene butadiene rubber, isoprene, multi rubber, stearic acid, sulfur, plasticizing powder, antioxidant and preservative, weight of each component as follows: styrene butadiene rubber 20 ~ 30, 20 ~ 25 Yuan rubber, isoprene from 5 to 8, stearic acid 5 ~ 8, sulfur 3 ~ 5, 10 ~ 20 plasticizing powder, antioxidant 5 ~ 10, 5 ~ 10 preservatives. The rubber material made by the formula of the invention has strong corrosion resistance, strong abrasion resistance, strong acid and alkali resistance, and is not easy to substitute reaction.
【技术实现步骤摘要】
用于市政工程领域且具有防滑耐腐蚀、耐磨的橡胶材料
本专利技术涉及橡胶材料
,具体涉及用于市政工程领域且具有防滑耐腐蚀、耐磨的橡胶材料。
技术介绍
橡胶应用在生活生产的各个领域当中,有些时候橡胶的工作环境比较艰苦,如果遇到强酸强碱会收到腐蚀而影响其性能,并影响大家的正常工作,目前的橡胶多采用化工原料制成,耐腐蚀、耐磨性通常有限,不利于生产生活。
技术实现思路
为了解决上述问题,本专利技术提供了用于市政工程领域且具有防滑耐腐蚀、耐磨的橡胶材料。本专利技术通过以下技术方案得以实现:一种用于市政工程领域且具有防滑耐腐蚀、耐磨的橡胶材料,由丁苯橡胶、多元橡胶、异戊二烯、硬脂酸、硫磺、塑化粉、防老剂、防腐剂组成,其组成包括以下质量份的组分:丁苯橡胶20~30份,多元橡胶20~25份,异戊二烯5~8份,硬脂酸5~8份,硫磺3~5份,塑化粉10~20份,防老剂5~10份,防腐剂5~10份。优选地,各组分的质量配比如下:丁苯橡胶25份,多元橡胶22份,异戊二烯6份,硬脂酸7份,硫磺3份,塑化粉15份,防老剂8份,防腐剂6份。本专利技术用于市政工程领域且具有防滑耐腐蚀、耐磨的橡胶材料,其组成还包括陶瓷基纳米复合材料1~5份。优选的,含有陶瓷基纳米复合材料的本专利技术的橡胶材料是由以下质量配比的组分制备:丁苯橡胶30份,多元橡胶20份,异戊二烯6份,硬脂酸5份,硫磺2.5份,塑化粉11份,防老剂7份,防腐剂6份、陶瓷基纳米复合材料3份。所述陶瓷基纳米复合材料1~5质量份是以碳化硅,氧化铝以及高岭土为原料制备得到的纳米复合材料,其粒径在50-200nm。相比于现有技术,本专利技 ...
【技术保护点】
一种用于市政工程领域且具有防滑耐腐蚀、耐磨的橡胶材料,其特征在于,包括以下质量份的组分:丁苯橡胶20~30份,多元橡胶20~25份,异戊二烯5~8份,硬脂酸5~8份,硫磺3~5份,塑化粉10~20份,防老剂5~10份,防腐剂5~10份。
【技术特征摘要】
1.一种用于市政工程领域且具有防滑耐腐蚀、耐磨的橡胶材料,其特征在于,包括以下质量份的组分:丁苯橡胶20~30份,多元橡胶20~25份,异戊二烯5~8份,硬脂酸5~8份,硫磺3~5份,塑化粉10~20份,防老剂5~10份,防腐剂5~10份。2.根据权利要求1所述的用于市政工程领域且具有防滑耐腐蚀、耐磨的橡胶材料,其特征在于:由以下质量配比的组分制备:丁苯橡胶25份,多元橡胶22份,异戊二烯6份,硬脂酸7份,硫磺3份,塑化粉15份,防老剂8份,防腐剂6份。3.根据权利要求1所述的用于市政工程...