The invention discloses a modified rubber material comprises the following raw materials: epoxidized natural rubber, polyurethane rubber, Shi Moxi, three phosphoric acid 2-butoxyethyl ester, adipic acid ester, three (2, 4 Di tert butyl phenyl) phosphite, acrylic acid, maleic anhydride grafted stearic acid ester, magnesium hydroxide, kaolin, glass beads, sixteen alkyl sulfonic acid calcium, two ethyl two dithiocarbamate zinc chloride, polyethylene, isoprene, brominated paraffin, polyvinyl chloride fiber, two methyl silicone oil, carbon fiber, polyamide fiber, carboxy ethyl cellulose, surfactant, initiator, chain extender, crosslinking agent, degassing agent, leveling agent, catalyst, accelerator, increasing plasticizer, dispersing agent, thickening agent, curing agent, antibacterial agent, antioxidant, light stabilizer, heat stabilizer, anti-aging agent, ultraviolet absorbent, flame retardant, anti Smoke agent. The material of the invention has good flame retardant effect, strong shock resistance and strong toughness, and can be widely used in the manufacture of tyres, rubber hoses, adhesive tapes, cables and the like, and has remarkable economic and social benefits.
【技术实现步骤摘要】
一种改性橡胶材料
本专利技术属于橡胶材料制备
，具体涉及一种改性橡胶材料。
技术介绍
橡胶（Rubber）：具有可逆形变的高弹性聚合物材料。在室温下富有弹性，在很小的外力作用下能产生较大形变，除去外力后能恢复原状。橡胶属于完全无定型聚合物，它的玻璃化转变温度（Tg）低，分子量往往很大，大于几十万。橡胶一词来源于印第安语cau-uchu，意为“流泪的树”。天然橡胶就是由三叶橡胶树割胶时流出的胶乳经凝固、干燥后而制得。1770年，英国化学家J.普里斯特利发现橡胶可用来擦去铅笔字迹，当时将这种用途的材料称为rubber，此词一直沿用至今。橡胶的分子链可以交联，交联后的橡胶受外力作用发生变形时，具有迅速复原的能力，并具有良好的物理力学性能和化学稳定性。橡胶是橡胶工业的基本原料，广泛用于制造轮胎、胶管、胶带、电缆及其他各种橡胶制品。橡胶按原料分为天然橡胶和合成橡胶。按形态分为块状生胶、乳胶、液体橡胶和粉末橡胶。乳胶为橡胶的胶体状水分散体；液体橡胶为橡胶的低聚物，未硫化前一般为粘稠的液体；粉末橡胶是将乳胶加工成粉末状，以利配料和加工制作。20世纪60年代开发的热塑性橡胶...
【技术保护点】
一种改性橡胶材料，其特征在于，以重量份为单位，包括以下原料：环氧化天然橡胶80‑101份、聚氨酯橡胶48‑60份、石墨烯45‑62份、磷酸三丁氧基乙酯26‑33份、己二酸酯15‑24份、三（2，4‑二叔丁基苯基）亚磷酸酯14‑23份、丙烯酸硬脂酸酯12‑15份、马来酸酐接枝16‑23份、氢氧化镁4‑6份、高岭土7‑10份、玻璃微珠5‑9份、十六烷基磺酸钙4‑8份、二乙基二硫代氨基甲酸锌5‑12份、氯化聚乙烯12‑16份、异戊二烯12‑16份、溴化石蜡14‑23份、聚氯乙烯纤维9‑15份、二甲基硅油8‑13份、碳纤维7‑12份、聚酰胺纤维4‑6份、羧乙基纤维素5‑9份、表面活...
【技术特征摘要】
1.一种改性橡胶材料，其特征在于，以重量份为单位，包括以下原料：环氧化天然橡胶80-101份、聚氨酯橡胶48-60份、石墨烯45-62份、磷酸三丁氧基乙酯26-33份、己二酸酯15-24份、三（2，4-二叔丁基苯基）亚磷酸酯14-23份、丙烯酸硬脂酸酯12-15份、马来酸酐接枝16-23份、氢氧化镁4-6份、高岭土7-10份、玻璃微珠5-9份、十六烷基磺酸钙4-8份、二乙基二硫代氨基甲酸锌5-12份、氯化聚乙烯12-16份、异戊二烯12-16份、溴化石蜡14-23份、聚氯乙烯纤维9-15份、二甲基硅油8-13份、碳纤维7-12份、聚酰胺纤维4-6份、羧乙基纤维素5-9份、表面活性剂0.6-1.2份、引发剂0.4-0.6份、扩链剂0.6-0.8份、交联剂0.3-0.5份、脱气剂0.3-0.4份、流平剂0.4-0.7份、催化剂0.2-0.4份、促进剂0.2-0.3份、增塑剂0.3-0.5份、分散剂0.2-0.4份、增粘剂0.3-0.4份、固化剂0.7-1.1份、抗菌剂0.6-1.2份、抗氧剂0.4-0.6份、光稳定剂0.2-0.4份、热稳定剂0.1-0.2份、抗老剂0.6-1.2份、紫外线吸收剂0.4-0.6份、阻燃剂1.2-1.5份、抑烟剂0.5-0.8份；所述分散剂为分散剂NC；所述增粘剂为丁基三甲氧基硅烷；所述固化剂为环氧类树脂固化剂；所述抗菌剂为碳酸锂；所述抗氧剂为抗氧剂1010；所述光稳定剂为光稳定剂770；所述热稳定剂为二盐基邻苯二甲酸铅；所述抗老剂为巴斯夫UV-234抗老剂;所述紫外线吸收剂为邻羟基苯甲酸苯酯；所述阻燃剂以重量份为单位，包括以下原料：乙二醇乙醚醋酸酯48-65份、无苯环氧树脂20-34份、脂肪醇聚氧乙烯醚硫酸铵18-25份、三季戊四醇12-22份、尿素10-16份、氧化铝7-12份、三氧化二锑9-12份、氧化锰5-9份、活性白土8-12份、渗透剂1.3-1.8份、增效剂0.8-1.2份；所述抑烟剂以重量份为单位，包括以下原料：三丁基氧化锡22-43份、氢氧化钼12-20份、高岭土10-16份、氧化铝6-12份、八钼酸铵4-7份、硬脂酸1.2-2份；所述改性橡胶材料的制备方法，包括以下步骤：S1：将石墨烯粉碎，过300-500目筛子，制得粉末，所得粉末在磁场强度为5830-6250GS，超声波功率为350-480W，温度为42-53℃，转速为200-300r/min下，搅拌22-36min，制得石墨烯能量粉末；S2：向步骤S1制得的石墨烯能量粉末中加入表面活性剂，在温度为63-74℃，转速为120-150r/min下活化0.9-1.4h，制得活化石墨烯能量粉末；S3：在氮气保护下，向步骤S2制得的活化石墨烯能量粉末中加入环氧化天然橡胶、聚氨酯橡胶、磷酸三丁氧基乙酯、己二酸酯、三（2，4-二叔丁基苯基）亚磷酸酯、丙烯酸硬脂酸酯、马来酸酐接枝...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。