适用于Na+离子污染吹泥冲填土的治理与固化水泥组合物制造技术
It is suitable for the treatment of Na+ ion contaminated dredger fill and a new formula of solidified cement
The invention discloses a method for Na+ ion pollution blowing mud rushed governance filling and new formula curing cement, which comprises the following components, as mass fraction of cement: 10, water 5.5, gypsum powder 0.5, composite admixture 0.825; the composite addition agent comprises the following components, as mass fraction: 1 calcium chloride, magnesium chloride and aluminum chloride in 1.5 copies, 1.5 copies, 1.5 copies of the alum material; alum material including alum and alum material using alum and green copperas mass ratio of 3:1 mixed into. By adopting the technical proposal, the new formula not only can obviously increase the effect of Na
【技术实现步骤摘要】
适用于Na+离子污染吹泥冲填土的治理与固化水泥新配方
本专利技术涉及土木工程
，具体涉及一种适用于Na+离子污染吹泥冲填土的治理与固化水泥新配方。
技术介绍
近几年，我国沿海地区从天津到珠海，海涂围垦工作轰轰烈烈，如浙江沿海地区的宁波、舟山、温州也正在开展沿海海涂围垦工作。沿海产业带开发已成为沿海当地政府的重点内容，目前各地的沿海产业带工作主要是海涂围垦与围垦后土地的利用。我国东南沿海海涂围垦地基处理方法较多，较为实用的是排水固结法，由于海涂面标高低而且海涂土承载力很低，为使海涂围垦而成的土地能用于工程建设，必须新造较厚的表层土，制造方法常用“吹砂法+排水固结法”，该法加固效果较好，但在东南滨海饱和软粘土地区(如浙江温州)，由于缺少砂料，吹砂法成本高，而改用“吹泥法+真空预压+塑料排水板”，该法已在实践中取得成功。但这些围垦冲填土因紧靠大海，而且所吹的泥均来自大海表层冲填淤泥，含有一定量的Na+离子，Na+离子的污染直接影响冲填土的化学结构成分，在常规的水泥土加固中抗压强度与抗剪强度明显比一般温州淤泥土差，而且Na+离子污染对建筑物底层混凝土质量有一定的侵蚀...
【技术保护点】
一种适用于Na+离子污染吹泥冲填土的治理与固化水泥新配方，其特征在于：包括以下组分，按质量分数计：
【技术特征摘要】
1.一种适用于Na+离子污染吹泥冲填土的治理与固化水泥新配方，其特征在于：包括以下组分，按质量分数计：所述复合外掺剂包括以下组分，按质量分数计：其中，矾料包括明矾和绿矾，矾料采用明矾和绿矾3：1的质量比混配而成。2.根据权利要求1所述的一种适用于Na+离子污染吹泥冲填土的治理与固化水泥新配方，其特征在于：所述生石膏粉为白色干粉，其中SO3含量为42.5％，比表面积3500cm2/g。3.根据权利要求1所述的一种适用于Na+离子污染吹泥冲填土的治理与固化水泥新配方，其特征在于：所述氯化钙为无水氯化钙，分子量110.99，白色粒状物，含量≥96.0％；所述氯化镁为六水合氯化镁，白色结晶体，含量≥98.0％；所述氯化铝为三氯化铝，分子量133.34，无色透明晶体，含量≥98.0％；明矾，无色透明结晶体，含量≥99.2％；绿矾，透明、淡绿色结晶体，含量≥97％。4...