The invention relates to the technical field of polycarbonate, especially an aging resistant polycarbonate composition, in accordance with the mass fraction meter comprises the following components: two acrylic ester 3-12 portions, nano titanium dioxide 3.5-6.8, isoamyl alcohol four 15-25, 10-20 mica, polysiloxane polycarbonate 5-12, glass fiber 2.6-4.2, polycarbonate 30-45, anti UV agent 12-18, octadecanamide 1.5-3.9. Using the above formula, the polycarbonate composition of the invention helps to enhance the liquidity and reduce the static power injection molding follow-up prepared, at the same time can enhance the effectiveness of the whole process and product quality; in addition, the invention of aging resistant polycarbonate compositions.
【技术实现步骤摘要】
本专利技术涉及聚碳酸酯
，特别是一种耐老化聚碳酸酯组合物。
技术介绍
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物，根据酯基的结构可分为脂肪族、芳香族、脂肪族-芳香族等多种类型。其中由于脂肪族和脂肪族-芳香族聚碳酸酯的机械性能较低，从而限制了其在工程塑料方面的应用。目前仅有芳香族聚碳酸酯获得了工业化生产。由于聚碳酸酯结构上的特殊性，现已成为五大工程塑料中增长速度最快的通用工程塑料。
技术实现思路
本专利技术需要解决的技术问题是提供一种耐老化聚碳酸酯组合物。为解决上述的技术问题，本专利技术的一种耐老化聚碳酸酯组合物，按照质量份数计包括以下组分：丙二酸酯3-12份，纳米二氧化钛3.5-6.8份，异戊四醇15-25份，云母10-20份，聚硅氧烷-聚碳酸酯5-12份，玻璃纤维2.6-4.2份，聚碳酸酯30-45份，抗紫外线剂12-18份，硬脂酰胺1.5-3.9份。进一步的，按照质量份数计包括以下组分：丙二酸酯3份，纳米二氧化钛3.5份，异戊四醇15份，云母10份，聚硅氧烷-聚碳酸酯5份，玻璃纤维2.6份，聚碳酸酯30份，抗紫外线剂12份，硬脂酰胺1.5份。进一步的，按照质量份数计包括以下组分：丙二酸酯12份，纳米二氧化钛6.8份，异戊四醇25份，云母20份，聚硅氧烷-聚碳酸酯12份，玻璃纤维4.2份，聚碳酸酯45份，抗紫外线剂18份，硬脂酰胺3.9份。进一步的，按照质量份数计包括以下组分：丙二酸酯5份，纳米二氧化钛4.3份，异戊四醇20份，云母13份，聚硅氧烷-聚碳酸酯8份，玻璃纤维3.4份，聚碳酸酯35份，抗紫外线剂13份，硬脂酰胺2.2份。进一...
【技术保护点】
一种耐老化聚碳酸酯组合物，其特征在于，按照质量份数计包括以下组分：丙二酸酯3‑12份，纳米二氧化钛3.5‑6.8份，异戊四醇15‑25份，云母10‑20份，聚硅氧烷‑聚碳酸酯5‑12份，玻璃纤维2.6‑4.2份，聚碳酸酯30‑45份，抗紫外线剂12‑18份，硬脂酰胺1.5‑3.9份。
【技术特征摘要】
1.一种耐老化聚碳酸酯组合物，其特征在于，按照质量份数计包括以下组分：丙二酸酯3-12份，纳米二氧化钛3.5-6.8份，异戊四醇15-25份，云母10-20份，聚硅氧烷-聚碳酸酯5-12份，玻璃纤维2.6-4.2份，聚碳酸酯30-45份，抗紫外线剂12-18份，硬脂酰胺1.5-3.9份。2.按照权利要求1所述的一种耐老化聚碳酸酯组合物，其特征在于，按照质量份数计包括以下组分：丙二酸酯3份，纳米二氧化钛3.5份，异戊四醇15份，云母10份，聚硅氧烷-聚碳酸酯5份，玻璃纤维2.6份，聚碳酸酯30份，抗紫外线剂12份，硬脂酰胺1.5份。3.按照权利要求1所述的一种耐老化聚碳酸酯组合物，其特征在于，按照质量份数计包括以下组分：丙二酸酯12份，纳...