The invention discloses a single component acrylic wood coatings, including water PG 1219 82; butyl carbitol 0.5; butyl carbitol /Dow51 5; Aquamat 208 3; BYK 346 0.4; RM 825 solution 1 Tego; 805 0.1; Acematt TS100 1.6 water; 5.5, the waterborne polyacrylate preparation of waterborne wood paint with low temperature film is good, good leveling, fullness, high wear resistance, good texture, anti chemical and anti tack excellent characteristics, but also with polyacrylate high adhesion, abrasion resistance, chemical resistance and flexibility.
【技术实现步骤摘要】
本专利技术涉及木器涂料
,具体地说是一种单组分聚丙烯酸酯木器漆。
技术介绍
丙烯酸涂料具有快干,耐光、耐候性优异等特点,目前其价格较低,在市场上广受关注,但传统的丙烯酸涂料成膜后,耐水性、抗回粘性以及柔韧性差。
技术实现思路
本专利技术的技术任务是解决现有技术的不足,提供一种单组分聚丙烯酸酯木器漆。本专利技术解决其技术问题所采用的技术方案是:一种单组分聚丙烯酸酯木器漆,包括以下组分且各组分重量分数比为:PG-121980-84份;丁基卡必醇0.2-0.8份;丁基卡必醇/Dow513-6份;Aquamat2081-5份;BYK3460.1-0.7份;RM825水溶液0.5-2份;Tego8050.1-0.3份;AcemattTS1001.2-2份;水4-7份。优选的,PG-121982份;丁基卡必醇0.5份;丁基卡必醇/Dow515份;Aquamat2083份;BYK3460.4份;RM825水溶液1份;Tego8050.1份;AcemattTS1001.6份;水5.5份。本专利技术的一种单组分聚丙烯酸酯木器漆配方与现有技术相比所产生的有益效果是:采用水性聚丙烯酸酯制备的水性木器漆具有低温成膜性好、流平性好、丰满度高、耐磨、手感好、抗化学品及抗回粘性优等特点,还具备聚丙烯酸酯的高附着力、耐磨、抗化学品性及柔韧性的特点。具体实施方式下面结合具体实施例详细说明本专利技术。实施例1:将PG-121982份;丁基卡必醇0.5份;丁基卡必醇/Dow515份;Aquamat2083份;BYK3460.4份;RM825水溶液1份;Tego8050.1份;Acematt ...
【技术保护点】
一种单组分聚丙烯酸酯木器漆,其特征在于,包括以下组分且各组分重量分数比为: PG‑1219 80‑84份;丁基卡必醇 0.2‑0.8份;丁基卡必醇/Dow51 3‑6份; Aquamat 208 1‑5份; BYK 346 0.1‑0.7份;RM 825 水溶液 0.5‑2份; Tego 805 0.1‑0.3份;Acematt TS100 1.2‑2份;水 4‑7份。
【技术特征摘要】
1.一种单组分聚丙烯酸酯木器漆,其特征在于,包括以下组分且各组分重量分数比为:PG-121980-84份;丁基卡必醇0.2-0.8份;丁基卡必醇/Dow513-6份;Aquamat2081-5份;BYK3460.1-0.7份;RM825水溶液0.5-2份;Tego8050.1-0.3份;AcemattTS1001.2-2...
【专利技术属性】
技术研发人员:李景茂,
申请(专利权)人:大连佳秀百隆新材料股份有限公司,
类型:发明
国别省市:辽宁;21