一种适合软质炭黑生产的耐磨送风风机制造技术
Wear resistant blower fan suitable for soft carbon black production
A blower is suitable for the production of soft carbon black in casing wear, (1) the inner and out of the wind at D322 electrode welding formation of surfacing layer (2), the impeller (3) with D322 electrode on the inner arc surface of the blade on the bead formation of surfacing layer (2), the utility model has the advantages of prolonging the chassis and the service life of the impeller, from the original 10~15 days, to extend the period of use now in more than 180 days, the original use of the 304 stainless steel material, wear into carbon black, because there is no magnetic, so no suction, and the use of materials, a magnetic separator, in the magnet the removal, improve the quality of the product.
【技术实现步骤摘要】
本技术涉及一种送风风机，尤其涉及一种适合软质炭黑生产的耐磨送风风机。
技术介绍
在年产能4万吨软质炭黑生产线上，炭黑的输送风机的过流部件的材质是304不锈钢，在使用过程中，由于软质炭黑产量大、粘性大，同时软质炭黑生成反应速度慢，更易产生焦粒等诸多原因，生产软质炭黑的送风风机，一般使用15~20天后，在风机出口处及叶轮中叶片磨损严重，发生炭黑泄漏和风机出力下降的状况，不符合连续性生产和工艺要求，停机维修降低了生产效率，增加了生产运行成本，并且影响生产现场的环境。
技术实现思路
本技术的目的在于提供一种适合软质炭黑生产的耐磨送风风机，解决了软质炭黑送风风机在使用过程中，一般使用15~20天后，在风机出口处及叶轮中叶片磨损严重，发生炭黑泄漏和风机出力下降的状况，不符合连续性生产和工艺要求，停机维修降低了生产效率，增加了生产运行成本，并且影响生产现场的环境的问题。本技术是这样实现的，它包括机壳、堆焊层、叶轮，其特征在于，在机壳内圈和出风处用D322焊条进行堆焊形成堆焊层，在叶轮上的叶片的内弧面上用D322焊条进行堆焊形成堆焊层。堆焊层的硬度为HB≥450。堆焊层的厚度为5mm。本技术的技术效果是：本技术延长了机壳和叶轮的使用寿命，从原15~20天，延长到现在使用期限在180天以上，原使用的304不锈钢材料，磨损后混入到炭黑中，因为没有磁性，所以无法吸除，影响了炭黑产品的质量，而现使用的材料，有一定的磁性，能在除铁器中经磁铁去除，提高了炭黑产品的质量。附图说明图1为本技术的结构示意图。在图中，1、机壳2、堆焊层3、叶轮。具体实施方式结合图1来具体说明本技术，在机壳（1...
【技术保护点】
一种适合软质炭黑生产的耐磨送风风机，它包括机壳（1）、堆焊层（2）、叶轮（3），其特征在于，在机壳（1）内圈和出风处用D322焊条进行堆焊形成堆焊层（2），在叶轮（3）上的叶片的内弧面上用D322焊条进行堆焊形成堆焊层（2）。
【技术特征摘要】
1.一种适合软质炭黑生产的耐磨送风风机，它包括机壳（1）、堆焊层（2）、叶轮（3），其特征在于，在机壳（1）内圈和出风处用D322焊条进行堆焊形成堆焊层（2），在叶轮（3）上的叶片的内弧面上用D322焊条进行堆焊形成堆...
【专利技术属性】
技术研发人员：付金华，侯少波，李核疆，赵双庆，程文辉，
申请(专利权)人：江西黑猫炭黑股份有限公司，
类型：新型
国别省市：江西;36