The invention discloses a method for preparing two poly acid polyol and its application in polyurethane foam. The present invention provides two polylactic acid polyol preparation method, is based on two polylactic acid and glycerol as raw material, with two lauric acid two octyl tin, zinc acetate, multi hydroxyl polyols esterification reaction of four butyl titanate as catalyst. The advantage of the two poly acid polyol of the invention is that the source material of the poly (two) acid polyol is wide, and can be extracted from common plants. The polyurethane foam prepared by the invention has the advantages of good mechanical property and excellent thermal insulation performance.
【技术实现步骤摘要】
本专利技术涉及一种生物基来源二聚酸多元醇的合成及在聚氨酯泡沫中的应用，属于可生物来源高分子材料领域。
技术介绍
聚氨酯泡沫是目前国际上性能最好的保温材料，主链含—NHCOO—重复结构单元的一类聚合物，英文缩写PU。由异氰酸酯(单体)与羟基化合物聚合而成，其生产过程是由多元醇和异氰酸酯以催化剂，发泡剂等助剂在适当的环境温度下，制得含有氨基甲酸酯基的闭孔泡沫。聚氨酯泡沫使用的多元醇主要为聚醚多元醇和聚酯多元醇，其由石油中提取，而石油是不可再生能源。面对目前资源日益短缺和社会不断进步的局面，这与当代可持续发展的需求与目标相违背。同时，人们对高分子材料的需求量越来越大，性能的要求也越来越高。然而，由于高分子材料的不易降解性，使其被广泛应用的同时，也给人们带来了一系列的环境污染和生态问题，因此尽快研究环境友好型的生物可降解材料愈加迫切。二聚酸是一种生物基来源的可生物降解高分子材料，是天然油脂的产物，具有毒性低，来源广泛且可再生等优点。同时由于二聚酸有两个羧基及两个较大的非极性羟基，其高度的分支结构和36个碳原子构成的长碳链使其拥有了良好的热稳定性能，高度的柔软性和超强的憎...
【技术保护点】
一种含有多羟基生物基来源的二聚酸多元醇，其特征在于由下列原料合成制备得到：二聚酸和丙三醇摩尔比例为1：1‑1：3；催化剂用量为二聚酸质量的0.1%‑2%；其中，催化剂为二月桂酸二丁基锡，钛酸四丁酯，醋酸锌。
【技术特征摘要】
1.一种含有多羟基生物基来源的二聚酸多元醇，其特征在于由下列原料合成制备得到：二聚酸和丙三醇摩尔比例为1：1-1：3；催化剂用量为二聚酸质量的0.1%-2%；其中，催化剂为二月桂酸二丁基锡，钛酸四丁酯，醋酸锌。2.权利要求1所述的一种含有多羟基生物基来源的二聚酸多元醇的制备方法，其特征在于按照下述方法进行：（1）称量：将二聚酸和丙三醇按照上述的比例称量，然后加入占二聚酸质量的0.1%-2%的催化剂；（2）二聚酸多元醇的制备：将步骤（1）中的反应通入氮气，机械搅拌转速为500r/min，同时在一侧加上分水器和冷凝管，以排除反应生成的水，使反应向正方向进行，设置温度140~160℃，测量酸值，当酸值达到1以下时，其反应完全，可以停止反应，烘干产物除去水分，制得的产物二聚酸多元醇。3.根据权利要求2所述的一种含有多羟基生物基来源的二聚酸多元醇的制备方法，其特征在于上述二聚酸多元醇的羟值范围是250-600mgKOH/g。4.权利要求1所述的一种含有多羟基生物基来源的二聚酸多元醇用于制备聚氨酯泡沫的方法，其特征在于其配方为：二聚...
【专利技术属性】
技术研发人员：杨荣，王波，李锦春，张鑫，
申请(专利权)人：常州大学，
类型：发明
国别省市：江苏;32