A hierarchical method of catalytic degradation of polyurethane materials is the first catalyst, water and polyurethane material mixed polyurethane degradation system; heat degradation reaction, after filtering, washing and drying, the degradation products of polyurethane; polyurethane degradation products added second with two times of catalyst degradation system, heating two degradation reaction the gas product, by distillation, condensation and collection after tetrahydrofuran, the remaining solid product after the reaction through washing, filtering and drying to obtain benzene derivatives. The invention has the advantages of low cost, mild recovery condition and high degradation activity.
【技术实现步骤摘要】
本专利技术属于高分子材料降解回收利用领域，具体涉及一种分层次催化降解聚氨酯材料的方法。
技术介绍
聚氨酯是一类重要的合成树脂，从化学结构上可以分为聚醚型和聚酯型聚氨酯，其中聚醚型聚氨酯主要由多异腈酸酯与聚醚多元醇共聚而成。它以优良的性能、多种产品形态、简便的成型工艺等优势应用广泛。它可以以泡沫塑料、弹性体、涂料、胶黏剂、纤维、防水材料以及铺装材料等多种产品形态应用于交通运输、建筑、机械、电子设备、合成皮革等诸多领域。其中，硬质聚氨酯泡沫塑料的导热系数比其它合成保温材料和天然保温材料都低，而且可以现场浇筑，快速成型，是用量越来越大的合成树脂保温材料，广泛应用于民用家电、管道保温及工业保温的领域；软质泡沫塑料以其弹性好、透气性良好等特点广泛用作床具、车船和家具座椅等的垫材；而聚氨酯弹性体则以耐磨、耐低温、高强度、耐油著称，作为特种合成橡胶用于制作矿山油田机械的各种橡胶零部件。我国在2014年的聚氨酯产量为938万吨，几乎占世界聚氨酯产量的一半，但是在聚氨酯行业飞速发展的同时，大量的边角料和废旧产品的处理和回收则是相关企业不得不面对的问题。废旧高分子材料的回收方法可分...
【技术保护点】
一种分层次催化降解聚氨酯材料的方法，其特征在于包括如下步骤：（1）将第一催化剂与水配成催化剂质量浓度为5～70%的反应溶液；（2）反应溶液与聚氨酯材料按100:1～200的重量比例混合，配成聚氨酯降解体系；（3）将配成的聚氨酯降解体系加热到50～250℃，进行降解10min～72h；（4）反应完成冷却后，降解体系经过滤、洗涤、干燥，得到的聚氨酯降解产物；（5）聚氨酯降解产物加入第二催化剂，按100:1～100重量比混合均匀配成二次降解体系；（6）将配成的二次降解体系加热到50～300℃进行二次降解，反应5min～36h；（7）反应期间气体产物经蒸馏、冷凝、收集后得到四氢呋喃...
【技术特征摘要】
1.一种分层次催化降解聚氨酯材料的方法，其特征在于包括如下步骤：（1）将第一催化剂与水配成催化剂质量浓度为5～70%的反应溶液；（2）反应溶液与聚氨酯材料按100:1～200的重量比例混合，配成聚氨酯降解体系；（3）将配成的聚氨酯降解体系加热到50～250℃，进行降解10min～72h；（4）反应完成冷却后，降解体系经过滤、洗涤、干燥，得到的聚氨酯降解产物；（5）聚氨酯降解产物加入第二催化剂，按100:1～100重量比混合均匀配成二次降解体系；（6）将配成的二次降解体系加热到50～300℃进行...
【专利技术属性】
技术研发人员：邓天昇，王玉琪，侯相林，齐永琴，
申请(专利权)人：中国科学院山西煤炭化学研究所，
类型：发明
国别省市：山西;14