人造透辉石材料及其制备方法技术

人造透辉石材料及其制备方法是一种人造纯透辉石晶体材料及其制备方法。该材料以硅砂、硫铁尾矿、高岭土、钠长石、石灰石、白云石等天然矿物为主要原料，经配料、熔制、成型、退火、核化、晶化等工艺步骤制得。制备该材料的配料化学组分及其重量百分比为：ＳｉＯ↓［２］４７～６１％，Ａｌ↓［２］Ｏ↓［３］４～９％，ＣａＯ１２～２０％，ＭｇＯ４～７％，ＴｉＯ↓［２］２～１５％，ＮａＯ↓［２］＋ＫＯ↓［２］３～７％，ＺｒＯ↓［２］１～４％，ＺｎＯ０～４％，Ｐ↓［２］Ｏ↓［５］１～４％，Ｆ１～３％，Ｃ１～３％。该纯透辉石晶体材料由微米级晶粒构成，致密度高，具有机械性能好、耐磨、耐腐蚀、抗冲击性能优异、无放射性等特性。（*该技术在2024年保护过期，可自由使用*）

Artificial diopside material and preparation method thereof

Artificial diopside material and preparation method thereof are artificial pure diopside crystal material and preparation method thereof. The material is composed of silica sand, pyrite tailing, kaolin, limestone, dolomite, albite, natural mineral as the main raw material, through mixing, melting, forming, annealing, nucleation and crystallization processes of preparation. Preparation of chemical ingredients of the material group and weight percentage: SiO down 2 from 47 to 61%, down Al 2 O down 3 4 ~ 9%, CaO12 ~ 20%, MgO4 ~ 7%, TiO: 2 2 ~ 15%, NaO: 2 KO: 2 from 3 to 7%, ZrO down 2 1 ~ 4%, ZnO0 ~ 4%, P: 2 O: 5 1 ~ 4%, F1 ~ 3%, C1 ~ 3%. The pure diopside crystal material is composed of micron size grains with high density, excellent mechanical properties, wear resistance, corrosion resistance, excellent shock resistance, and no radioactivity.

【技术实现步骤摘要】

本专利技术涉及一种人造透辉石型材及其制备方法，特别是采用非透辉石的矿物原料为主要原料制备透辉石型材的工艺方法。本专利技术属于矿物材料领域。
技术介绍
透辉石(Diopside)为单链状的硅酸盐矿物，结构式为CaMg，其中Mg2+经常可被其它离子所取代，如Fe2+、Fe3+、Al3+、Cr3+等，从而形成Ca(Mg2+，Fe2+，Fe3+，Al3+)的固溶体。透辉石的理论化学组成为SiO255.6％，CaO 25.9％，MgO 18.5％，属单斜晶系，晶体为短柱状，集合体呈粒状或放射状，多见浅绿色或浅灰色，玻璃光泽，硬度5.5～6，熔点1391℃，不溶于水和盐酸，密度3.27～3.38g/cm3。天然透辉石常含有Cr、Mn、Fe、V等杂质，透辉石化学稳定性好，不溶于HCl，耐磨性好，不含有机物，无结晶水。天然透辉石来源于透辉石岩，透辉石岩是一种多矿物组成岩，除透辉石外，透辉石岩往往还含有硅灰石、石英、方解石、透闪石、磷灰石、长石、方柱石、黑云母、榍石、石榴石等矿物。因此，自然界中除宝玉石外，少见纯透辉石。透辉石岩因其分布广泛、价廉、用途大而日益受到人们的重视。首先，作为陶瓷原料，透本文档来自技高网...

【技术保护点】
一种人造透辉石材料，其特征在于该材料为纯透辉石相，由微米级透辉石晶粒构成。

【技术特征摘要】