本发明专利技术涉及用复合材料制作仿陶瓷花盆的生产工艺及方法。该生产工艺及方法：分一、配料，二、铸模灌浆，三、真空处理，四、脱模检验及五、上高光冷瓷，五大步骤。用该工艺方法生产的仿陶瓷花盆，不仅外形美观，大可与陶瓷花盆相媲美，并且仿陶瓷花盆更具备了陶瓷花盆所没有的优点，它不用粘土，不消耗能源，它制造简单，质轻不易破碎，它运输方便，经久耐用，它是陶瓷产品更新换代的好新品，具有极大的市场及实用价值。

Process and method for making ceramic imitated flowerpot with composite material

The invention relates to a production process and a method for making a ceramic imitated flowerpot with composite material. The production process and method: divided into one, batching, two, casting grouting, three, vacuum treatment, four, release test and five, high gloss cold porcelain five steps. Imitation ceramic pot is produced with the process, not only beautiful appearance, can be comparable with ceramic pots, and imitation ceramic flowerpot has more advantages of ceramic pots do not have, it is not clay, no energy consumption, it has the advantages of simple manufacture, light weight and not easily broken, the transportation is convenient, durable, it is new good ceramic product renewal, has great practical value and market.

【技术实现步骤摘要】

本专利技术涉及仿陶瓷花盆的生产工艺及方法，尤其是用。
技术介绍
目前，陶瓷生产的花盆已在全世界长期普及使用，近年来，由于人们重视环保绿化的原因，其花盆的用量大量增加，大有供不应求之感，但是，制作陶瓷花盆需用宝贵的泥土资源，并且还要消耗不可再生的能源，尤其是一些大型花盆，其烧制难度又很大，致使其陶瓷花盆的成本及价格不断攀升，这样，就大大限制了陶瓷花盆的大量普及及使用，目前对此还没有很好的解决办法。
技术实现思路
为了解决制作陶瓷花盆需要宝贵的粘土及能源等问题，本专利技术提供了一种复合材料制作仿陶瓷花盆的制造工艺及生产方法，用该工艺及方法生产的仿陶瓷花盆，不仅外形美观，大可与陶瓷花盆相媲美，并且仿陶瓷花盆更具备了陶瓷花盆所没有的优点，它不用粘土，不消耗能源，它制造简单，它质轻不易破碎，方便运输，经久耐用，它是陶瓷产品更新换代的好新品，具有极大的市场及实用价值。本专利技术解决其技术问题所采用的方案是该生产工艺及方法分一·配料，二·铸模灌浆，三·真空处理，四·脱模检验及五·上高光冷瓷，五大步骤。以下详细说明一·配料轻煤粉45±1％，碳酸钙5±0.5％，水玻璃5±0.5％，玻璃纤维7±0.5％本文档来自技高网...

【技术保护点】
复合材料制作仿陶瓷花盆的生产工艺及方法，其特征是分一.配料，二.铸模灌浆，三.真空处理，四.脱模校验及五.上高光冷瓷，五大步骤做成；其具体工艺及方法如下：一.配料：轻煤粉４５±１％，碳酸钙５±０．５％，水玻璃５±０．５％，玻璃纤维７±０．５％，氧化铝３±０．５％，石英粉１０±１％，氧化铬绿１±０．５％及鲁片液２０±１，把以上配料顺序倒入料罐中搅拌均匀，成浆状料时待用。