Manufacturing method of a powder polymer cement modifier, the steps are, according to weight ratio, the first 0.1 to 2.5 parts of sodium sulfate, zinc stearate 0.1 - 2, 0.5 - 5, sodium silicate and sodium chloride in 0.5 ~ 1.5 and 0 ~ 5 phr silica mixed and crushed to the size less than 100, then the mixture of pulverized and ethylene vinyl acetate copolymer redispersible powder from 50 to 100, 10 to 30 portions of quartz sand and fly ash from 0 to 15, 0 to 10 portions of methyl cellulose ether and silane modified polymer powder 0 ~ 25 mix. The addition amount is 1.5% to 10% of the weight of the cement used, and compared with the present liquid macromolecule cement modifier, the storage and transportation is convenient, and the modification effect is better. The utility model can be widely used for the cement pavement, the airport, the underground waterproof project, the traffic culvert, the ship wharf, the water conservancy project and the civil building, etc., so as to make the project waterproof and leak, and prolong the service life.
【技术实现步骤摘要】
本专利技术属于高分子复合材料的水泥添加剂，即粉体高分子水泥改性剂的制作方法。
技术介绍
高分子水泥改性剂掺入混凝土和水泥砂浆中能使其内部结构更为紧密而富有韧性，从而使水泥制品、制件的抗渗水性、抗龟裂性、抗冲击性、耐磨性、耐酸碱性等理化性能显著提高，并能有效地改善其施工性能，兼有促凝、早强的效果。目前高分子水泥改性剂产品有两类，一类是以天然及天然改性高分子为主料，如松香、木质素磺酸盐的高分子水泥改性剂产品，另一类是以合成高分子为主料，如乙烯——醋酸乙烯共聚物的高分子水泥改性剂产品，后者的改性效果明显优于前者，且两者均为液体，即为液体高分子水泥改性剂。对于液体高分子水泥改性剂，其主要缺陷是贮运不方便，贮运效率不高，因为固含量仅50％左右，保质期较短，仅6个月左右，并需要额外加入防腐剂、防霉剂等有毒性助剂，这些缺陷在温差变化较大的环境里尤为明显。
技术实现思路
为了克服液体高分子水泥改性剂的上述缺点，我们研制了粉体高分子水泥改性剂。该改性剂百分百的固含量，不含防腐剂、防霉剂，保质期长，可达两年以上，环境温度变化不影响其贮运稳定性，完全克服了液体高分子水泥改性剂的缺陷。这...
【技术保护点】
一种粉体高分子水泥改性剂的制作方法，其特征是：一、按下述物料的重量比准备：①乙烯－醋酸乙烯共聚物可再分散乳胶粉５０．０～１００．０份②石英砂，４０－８０目 １０．０～３０．０份③粉煤灰，４０－１００目 ０～１５．０份④甲基纤维素醚 ０～１０．０份⑤硅烷改性聚合物粉０～２５．０份⑥硫酸钠０．１～２．５份⑦硬脂酸锌０．１～２．０份⑧硅酸钠０．５～５．０份⑨氯化钠０．５ ...
【技术特征摘要】
【专利技术属性】
技术研发人员：周诗彪，周光明，张维庆，张儒祥，
申请(专利权)人：湖南文理学院，
类型：发明
国别省市：43[中国|湖南]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。