一种保温隔热材料及其制备方法技术

本发明专利技术公开了一种新的保温隔热材料及其制备方法，该保温隔热材料主要由以下重量份的原料组成：珍珠岩２０～７０份、纤维２～１５份、氧化镁１５～７０份、硫酸镁５～２０份、氯化镁２～８份、发泡剂０．５～２份、粘结剂２～１５份、尿醛树脂１０～８０份。试验证实，本发明专利技术保温隔热材料具有优异的保温、隔热、防火、抗压、防潮、隔音性能，遇水不分散，能够广泛的应用于建筑、化工、仓储、及各种高低温管道等领域中。

Heat insulation material and preparation method thereof

The present invention discloses a new kind of heat insulating material and a preparation method thereof, wherein the thermal insulation material mainly consists of the following parts by weight of raw materials: 20 to 70 portions of perlite and fiber 2 - 15, 15 - 70, Magnesium Oxide Magnesium Sulfate 5 - 20, 2 - 8, magnesium chloride foaming agent 0.5 ~ 2, 2 to 15 portions of binder and urea formaldehyde resin 10 ~ 80. The test confirmed that the invention of insulation materials with thermal insulation, fireproof, moistureproof, sound insulation performance, non dispersed in water, can be widely used in construction, chemical industry, warehousing, and all kinds of high temperature pipeline etc..

【技术实现步骤摘要】

本专利技术涉及一种保温隔热材料，尤其涉及一种主要以珍珠岩为材料制备而成的保温隔热建筑材料及其制备方法和用途。
技术介绍
目前，市场上常见的保温隔热材料主要有如下几种膨胀珍珠岩材料、聚苯颗粒复合硅酸盐材料、粉煤灰陶粒材料等。我国生产膨胀珍珠岩保温材料已有30年的历史，年产量已达600万m3，但品种始终是单一的多孔结构产品。膨胀珍珠岩为一种外形极不规则，表面有许多孔洞、缝隙，凸凹不平和表面不连贯的粒状产品，这种结构特征使材料易碎，压缩比大，强度低，而且由于多孔，其吸水率可以高达500％，这些缺点大大降低了膨胀珍珠岩的保温性能及使用寿命。
技术实现思路
本专利技术所要解决的技术问题是克服现有技术的不足，提供一种具有优异保温性能的建筑材料。本专利技术所要解决的技术问题是通过以下技术途径来实现的一种保温隔热材料，主要有以下重量份的原料制成珍珠岩20～70份、纤维2～15份、氧化镁15～70份、硫酸镁5～20份、氯化镁2～8份、发泡剂0.5～2份、粘结剂2～15份、尿醛树脂10～80份。优选为珍珠岩62份、纤维3份、氧化镁20份、硫酸镁8份、氯化镁2份、发泡剂0.5份、粘结剂8份、尿醛树脂20份本文档来自技高网...

【技术保护点】
一种保温隔热材料，主要由以下重量份的原料组成：珍珠岩２０～７０份、纤维２～１５份、氧化镁１５～７０份、硫酸镁５～２０份、氯化镁２～８份、发泡剂０．５～２份、粘结剂２～１５份、尿醛树脂１０～８０份。