一种硬化水泥基材料防干缩开裂用纤维材料及其制备方法技术

本发明专利技术属于材料科学与工程科学技术领域，具体涉及一种硬化水泥基材料（水泥净浆、砂浆、混凝土及其复合材料）防干缩开裂用纤维材料，由有机合成纤维、无机纤维或有机无机混杂纤维和改性剂组成。本发明专利技术防裂纤维可对水泥基材料硬化后的干燥失水收缩开裂有很好的抑制减少作用，较之不掺者可使干缩裂缝减少４０－８５％，且对材料的和易性、抗压强度、抗折强度等不产生明显不良影响，本发明专利技术可广泛应用于水泥基材料工程，如水泥混凝土路面、桥面、地坪、护坡、大坝、墙体抹面等工程中，以提高工程质量和使用寿命。

Fiber material for preventing drying shrinkage cracking of hardened cement based material and preparation method thereof

The invention belongs to the technical field of materials science and engineering, in particular relates to a cement-based materials (cement paste, mortar, concrete and composite materials) anti dry shrinkage cracking with fibrous material, composed of organic synthetic fiber, inorganic fiber or organic inorganic hybrid fiber and modified agent. The invention of fiber cracking of cement-based materials hardening after drying shrinkage cracking has a good inhibiting effect is not reduced, the mixing can make the shrinkage cracks reduced by 40 - 85%, and the material workability, compressive strength, flexural strength, and has no obvious adverse effect, the invention can cement based materials are widely used in Engineering, such as cement concrete pavement, bridge deck, floor, wall, dam slope, surface engineering, in order to improve the engineering quality and service life.

【技术实现步骤摘要】

本专利技术属于材料科学与工程科学
，具体涉及一种防止硬化水泥基材料(水泥净浆、砂浆、混凝土及其复合材料)干燥失水收缩开裂的纤维材料。
技术介绍
水泥混凝土材料是当今世界上用量最大，使用最广泛的人造建筑材料之一。2004年我国水泥年产量已达8.6亿吨，每年水泥混凝土用量已达20亿立方米。在今后相当长的一段时间内，水泥混凝土仍将是我国现代工程建设的主要建筑材料。并且，由于其具有适用范围广，价格便宜，易浇注成型，比较耐久，还可有效利用一些工业固体废料制作节能环保型建筑材料等优点，而在众多建筑工程领域中发挥其它材料无法替代的作用。但是水泥混凝土也具有抗拉强度低，极限拉应变小，抗冲击强度差，易于失水收缩开裂等缺点，尤其是由于干燥失水造成混凝土收缩开裂使工程外观、使用功能、使用寿命等受到很大影响，且目前国内外均无很好的应对措施，使得研究专利技术硬化水泥基材料的防裂材料变得十分重要。水泥混凝土一旦失水收缩开裂，将极大地影响其抗渗、抗冻、抗化学介质侵蚀、抗钢筋锈蚀等性能，造成混凝土使用寿命大大缩短，混凝土维护修复费用大量上升，一旦路面开裂，将严重影响路面使用性能，修复十分困难，费用巨大，据本文档来自技高网...

【技术保护点】
一种硬化水泥基材料防干缩开裂用纤维材料，其特征在于：由有机合成纤维、无机纤维或有机无机混杂纤维和改性剂组成，其组份的体积百分比如下：有机合成纤维０～５５％无机纤维１０～７０％改性剂２～３０％　 　总量满足１００％。

【技术特征摘要】

【专利技术属性】
技术研发人员：马一平，
申请(专利权)人：同济大学，
类型：发明
国别省市：31[中国|上海]