Biological ceramsite filter material and preparation method thereof, belong to the field of water treatment engineering. In view of the existing ceramic filter with low porosity, especially micro content and low surface roughness, poor hydrophilicity caused by small specific surface area, adsorption ability, microbial immobilization, small amount of fixed rate is low, the biological ceramsite from 30 ~ 40wt.%, 30 ~ 45wt.% Shale Fly Ash, 10 to 20wt.% sludge, 3 ~ 8wt.% 0.5 ~ 2wt.% of pore forming agent and binder, the preparation method is as follows: mixing, forming, drying, roasting, sintering, modified. The invention can use large amount of industrial waste, the lowest energy load preparation; microbial adsorption can make the filter into a synergistic effect of adsorption and biodegradation in the surface immobilization, improve the degradation ability of organic matter; through surface chemical modification, so that the surface is positively charged and hydroxylation, have for the removal of natural organic matter in raw water.
【技术实现步骤摘要】
本专利技术属于水处理工程领域，涉及一种用于饮用水过滤技术以及原水的生物预处理、污水的深度处理的载体。
技术介绍
目前，在生物处理中常用的颗粒载体多为活性炭、沸石和陶粒等。这些生物载体存在的问题是(1)活性炭虽然具有巨大的比表面积，吸附能力极强，但是活性炭的强度低、寿命短、不宜冲洗、处理费用高等。(2)沸石由于孔径过大而造成比表面积小、吸附能力差。(3)目前常用的陶粒也存在很多缺陷孔隙率低，尤其是微孔含量低以及表面粗糙度不足、亲水性差，从而造成陶粒的比表面积过小，吸附性能差，因而微生物固定量小、固定化速率低，导致水处理效率低，净化效果差；由于比重不合理造成陶粒在生物滤池中不易形成流化状态，导致处理效率低；由于结构力不足，即坚硬度低、易碎，导致生物陶粒滤床的空隙度不合理，曝气气泡阻力增加，处理效率降低。上述原因造成目前的生物滤料使用成本高、处理效果差、净水效率低，故工程普及范围小。
技术实现思路
针对现有的陶粒滤料孔隙率低，尤其是微孔含量低、表面粗糙度不足、亲水性差而引起的比表面积小、吸附能力差、微生物固定量小、固定化速率低的问题，本专利技术提供一种可以取代活性炭生物...
【技术保护点】
生物陶粒滤料，其特征在于所述滤料由３０～４０ｗｔ．％页岩、３０～４５ｗｔ．％粉煤灰、１０～２０ｗｔ．％污泥、３～８ｗｔ．％成孔剂和０．５～２ｗｔ．％粘结剂制成。
【技术特征摘要】
【专利技术属性】
技术研发人员：冯奇，马放，邱珊，沃原，
申请(专利权)人：哈尔滨工业大学，
类型：发明
国别省市：93[中国|哈尔滨]