一种超细碳氮化钛粉及其制备方法技术

一种超细碳氮化钛粉及其制备方法，属于纳米陶瓷粉体制备技术领域，本发明专利技术的超细碳氮化钛粉，采用淀粉或蔗糖为碳源，氢化钛为钛源，其重量百分比是：淀粉或者蔗糖为５～３０％，氢化钛为７０～９５％，其余为氮气，其工艺方法是：（１）配料；（２）球磨；（３）干燥；（４）烧结；（５）取粉，本发明专利技术具有生产工艺简单、安全环保、不污染环境，并且生产原料来源广泛、生产效率高和成本低等优点，在工业化生产中具有较广阔的应用前景，适合于规模化生产，生产的超细碳氮化钛粉为棕红色，粒径在１００纳米以下。

Superfine carbon titanium nitride powder and preparation method thereof

A kind of superfine titanium carbonitride powder and its preparation method, preparation of nanometer ceramic powder system belongs to the technical field, ultrafine titanium carbonitride powder of the invention, using starch or sucrose as carbon source, titanium hydride as titanium source, its weight percentage is: starch or sucrose at 5 ~ 30%, 70 ~ 95% titanium hydride. For the rest of the nitrogen, its process is: (1) ingredients; ball milling; (2) (3) (4) drying; sintering; (5) take the powder, the invention has the advantages of simple production process, safety and environmental protection, no pollution to the environment, and the production of raw materials widely, high production efficiency and low cost. Has a wide application prospect in industrial production, suitable for large-scale production, the production of ultrafine titanium carbonitride powder is brown red, particle size below 100 nm.

【技术实现步骤摘要】

本专利技术属于纳米陶瓷粉体制备
，特别涉及。
技术介绍
碳氮化钛是一种性能优良，用途广泛的非氧化物材料，它具有熔点高、硬度大、耐腐蚀和抗氧化性好 特点，适用于机械化工，汽车制造和航空航天等许多领域。Ti(C，N)材料在金属切削刀具中得到广泛的应用，Ti(C，N)基硬质合金刀具强度高，硬度大，抗氧化性好，热传导性也较高。在金属切削加工中，Ti(C，N)还能生成相对较高的自由焓，增加其抵抗切削瘤、起皮和陷穴的形成。因此采用Ti(C，N)基硬质合金刀具高速研磨，在粗加工、半加工工件的尺寸精度和加七表面质量都优于WC或TiC基硬质合金刀具所加工的工件。由于TiC和TiN都具有NaCl型晶体结构，属于立方晶系面心立方点阵结构，Ti原子和C原子(对于TiN来说是N原子)各位于面心立方点阵的结点位置上，这两个点阵相距1/2的晶胞边长。TiC的晶胞参数为4.320A，而TiN的晶胞参数为4.235A，TiC的晶胞参数略小于TiC的晶胞参数。由于TiC和TiN属类质同型结构，TiC点阵中的C原子可以被N原子以任何的C或N原子Ti原子比例替代。因而，可以制备一种连续固溶体TiC1-xNx，0≤本文档来自技高网...

【技术保护点】
一种超细碳氮化钛粉，其特征是，采用淀粉或者蔗糖为碳源，氢化钛为钛源，其重量百分比是：淀粉或者蔗糖为５～３０％，氢化钛为７０～９５％，其余为氮气。