一种利用金矿尾矿制备Ca-α-Sialon材料的方法技术

一种利用金矿尾矿制备Ｃａ－α－ＳｉＡｌＯＮ材料的方法，属于陶瓷材料技术领域。工艺为：粉碎、配料、混合球磨、干燥制样、烧结和去除残留碳元素。最终得到主晶相为Ｃａ－α－ＳｉＡｌＯＮ，次晶相为ＳｉＣ的陶瓷粉体。本发明专利技术的优点在于：得到纯度较高的Ｃａ－α－ＳｉＡｌＯＮ陶瓷粉体，可广泛应用于冶金、化工、电力、能源等工业领域，工艺操作简单，成本低，对实现尾矿的综合利用有很重要的意义。

Method for preparing Ca- alpha -Sialon material by using gold mine tailings

A method of producing Ca alpha SiAlON material utilization of gold tailings system, belongs to the technical field of ceramic material. The process includes crushing, batching, mixing, ball milling, drying, sample preparation, sintering and removal of residual carbon elements. Finally, the main crystalline phase is Ca - SiAlON, and the secondary crystal phase is SiC. The invention has the advantages that the Ca alpha SiAlON ceramic powder with high purity, can be widely used in metallurgy, chemical, electric power, energy and other industries, technology has the advantages of simple operation, low cost, and has very important significance for the comprehensive utilization of tailings.

【技术实现步骤摘要】

本专利技术属于陶瓷材料
，提出了一种用金矿尾矿制备Ca-α-SiAlON材料的方法，具有较强的可行性。
技术介绍
在黄金生产过程中，尾矿一般以废水和固体矿渣混合物的形式存放于尾矿库中，在占用大量土地的同时，浪费了宝贵的矿产资源，严重影响生产环境；尾矿库还存在着极大的安全隐患，尾矿中的残液对生态环境的危害更大。黄金矿石有价元素含量很少，经选冶后产生比其它金属矿石更多的尾矿。随着“十一五”国家提倡国民经济协调发展和保护生态环境以来，黄金尾矿综合利用技术近年得到进一步重视。Ca-α-SiAlON材料具有优异的化学稳定性、高强度、高硬度、高韧性及高温机械性能，这些综合技术性能优于大多数钢及合金，因而在很多领域得到广泛的应用。比如可用作研磨介质、金属切削刀具、非铁合金管或丝的控制磨具、引擎及透平材料、耐火材料的结合剂等，目前Ca-α-SiAlON材料的制备方法主要为碳热还原氮化法，该方法是以碳(如碳黑、石墨等)作为还原剂，加入硅铝钙原料等，经充分混合，在1350℃到1800℃(温度因原料和成品不同而异)常压流动氮气下烧结，制备Ca-α-SiAlON材料。这种方法，适合纯度较高的原料，本文档来自技高网...

【技术保护点】
一种用金矿尾矿制备Ｃａ－α－ＳｉＡｌＯＮ材料的方法，其特征在于：工艺步骤为：ａ、粉粹：将金矿尾矿经磨矿，过筛，使尾矿粒度小于０．０７４ｍｍ；ｂ、配料、球磨混合：将金矿尾矿、硅砂、莫来石、碳粉按照１０∶（３０～３４）∶（１３～ １６）∶（３０～３２）质量百分比混合，将配制好的混合料放入氧化铝球磨罐中，用无水乙醇作为介质，球磨２２～２６小时，以达到细化粉体和混匀配料的目的；ｃ、烘料、制样：将上述料将在５０～７０℃的条件下烘干，再进行干燥混合３～５小时，以确定 混合物料的性质均匀，将混合好的物料放入钢膜中，于１３０－１５０ＭＰａ下单轴向机压成小圆坯；ｄ、烧...

【技术特征摘要】

【专利技术属性】
技术研发人员：徐利华，毕松梅，姚云，