本发明专利技术公开了一种高比表面硅氧碳陶瓷纳米管的制备方法，包括下列步骤：ａ．选用多孔氧化铝作为模板浸入到聚硅氧烷液体中；ｂ．浸过聚硅氧烷液体的模板在马弗炉中５０～６００℃温度下放置１～１０小时；ｃ．用酸去除氧化铝模板得到聚硅氧烷纳米管的前驱体；ｄ．将前驱体置于高温管式炉中在惰性气体保护下以２～１０℃／ｍｉｎ的升温速度将温度升至１０００～１５００℃，然后恒温０．５～４小时得到产物。本发明专利技术以氧化铝作为模板制备硅氧碳陶瓷纳米管，制备出孔道分布均匀、形状高度均匀有序的纳米材料，该材料比表面高达７００－２５００ｍ↑［２］／ｇ，可作为功能材料或载体在光电、催化等方面得到广泛应用。

Method for preparing high specific surface silicon oxygen carbon ceramic nano tube

The invention discloses a method for preparing high specific surface siloxicon ceramic tube, which comprises the following steps: A. using porous alumina membrane as template into polysiloxane liquid; B. soaked in liquid silicone template in a muffle furnace 50 to 600 DEG for 1 to 10 hours; the precursor C. acid removal of alumina the template polysiloxane nanotube; D. precursor in high temperature tube furnace under the protection of inert gas to 2 to 10 DEG C / min heating rate the temperature rose to 1000 to 1500 DEG C, then a constant temperature of 0.5 ~ 4 hours to obtain the product. Preparing siloxicon ceramic nanotube templates for the invention to alumina is prepared, pore distribution, shape of highly uniform ordered nanomaterials, the material surface is up to 700 - 2500m = 2 / g, can be used as functional material or carrier has been widely used in optoelectronics, catalysis etc..

【技术实现步骤摘要】

【技术保护点】
一种高比表面硅氧碳陶瓷纳米管的制备方法，包括下列步骤：ａ．选用平均孔径为２００ｎｍ、厚度为６０ｕｍ规格的多孔氧化铝作为模板，然后将上述模板浸入到聚硅氧烷液体中，所述聚硅氧烷液体选自单一的聚苯基甲基硅氧烷溶液或氢甲基硅油和乙烯基聚硅氧 烷的混合溶液；ｂ．将浸过聚硅氧烷液体的氧化铝模板在马弗炉中５０～６００℃温度下放置１～１０小时，使模板中的聚硅氧烷热固化；ｃ．用酸去除氧化铝模板得到聚硅氧烷纳米管的前驱体；ｄ．将上述聚硅氧烷纳米管的前驱体置于高温管式 炉中在惰性气体保护下，以２～１０℃／ｍｉｎ的升温速度将温度升至１０００～１５００℃，然后恒温０．５～４小时即得硅碳氧陶瓷纳米管，该硅氧碳陶瓷纳米管的比表面积为７００～２５００ｍ↑［２］／ｇ。

【技术特征摘要】

【专利技术属性】
技术研发人员：万传云，
申请(专利权)人：上海应用技术学院，
类型：发明
国别省市：31[中国|上海]