The invention discloses a process for producing aluminium chromium slag high grade refractory material, 1) aluminum chromium slag removal after crushing; 2) aluminum chromium slag crushed by acid leaching; 3) of aluminum chromium slag rinse water after acid leaching; 4) dehydration; drying; 5) 6 product packaging). The invention has the advantages that the invention is used to purify pickling method, the aluminum chromium slag in Na: 2 O reduced to 0.5%, down Fe 2 O down 3 reduced to below 1%, made of refractory refractory products reach more than 1700 DEG C, small shrinkage that is not easy to crack, can be used for producing high-grade refractory products, such as can be made into honeycomb ceramics, high Kangzha refractory products; two is the treasure, solves the chromium metal production enterprises aluminum chromium slag, occupy the field, the problem of environmental pollution, save resources, reduce the cost of production.
【技术实现步骤摘要】
本专利技术涉及一种用铝铬渣制作耐火材料的生产工艺。
技术介绍
在金属铬的冶炼生产中,每生产一吨金属铬就要产生二吨的冶炼炉渣,俗称铝铬渣,这种炉渣虽然有些被用作耐火材料,但由于含有较高的Fe2O3、Na2O有害杂质,Fe2O3在1.5%以上,Na2O在2%以上,用这种铝铬渣作为耐火材料制成的耐火制品耐火度不高,收缩大,易开裂,抗热震性能差,只能用作生产低档耐火制品。
技术实现思路
本专利技术的目的是提供一种用铝铬渣制成高级耐火材料的生产工艺。本专利技术的目的是通过如下方式实现的一种用铝铬渣制成高级耐火材料的生产工艺,其特征在于1)、将铝铬渣除杂后粉碎;2)、将粉碎后的铝铬渣用酸浸;3)、对酸浸后的铝铬渣用水漂洗;4)、脱水;5)、干燥;6)、成品包装本专利技术具有如下的有益效果,一是本专利技术采用酸洗去杂提纯法,使铝铬渣中的Na2O降低到0.5%以下,Fe2O3降低到1%以下,制成的耐火制品耐火度达到1700℃以上,收缩小,不易开裂,可以用作生产高级耐火制品,如能制成蜂窝陶瓷,高抗渣性耐火制品等;二是变废为宝,解决了金属铬生产企业铝铬渣堆放,占场地,污染环境的问题,节约了资源,降低了生产成本。具体实施例方式下面结合实施例对本专利技术做进一步说明取冶炼厂冶炼金属铬后产生的铝铬渣废料1)首先去杂粉碎;2)、将粉碎后的铝铬渣用盐酸浸泡除去铝铬渣中的Fe2O3、Na2O,Fe2O3、Na2O与盐酸反应生成FeCl3、NaCl,3)、对酸浸后的铝铬渣用水漂洗数次;使FeCl3、NaCl充分溶于水中;4)、脱水;5)、干燥;6)、成品包装。权利要求1.一种用铝铬渣制成高 ...
【技术保护点】
一种用铝铬渣制成高级耐火材料的生产工艺,其特征在于: 1)、将铝铬渣除杂后粉碎; 2)、将粉碎后的铝铬渣用酸浸; 3)、对酸浸后的铝铬渣用水漂洗; 4)、脱水; 5)、干燥; 6)、成品包装。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。