The invention discloses a crystallization type waterproof, thermal insulation mortar, which is characterized in that: 100 per kg powder with 480 to 600 liters of insulation materials are mixed into pellets by powder and heat insulation, the powder in the weight of raw materials: 425 cement 550 ~ 625 ~ 175, quartz sand 250, calcium carbonate 150 ~ 160, 85 ~ 100 ash, 4 to 7 portions of cellulose, polypropylene monofilament fiber of 3 to 5 copies, redispersible powder 21 ~ 29, the activity of cement based permeable crystallization masterbatch 13 ~ 17. The daub has good air permeability, thermal insulation property and fireproof property, and is not easy to crack, crack and fall off.
【技术实现步骤摘要】
本专利技术涉及一种建筑材料,具体来说是建筑墙面材料。
技术介绍
目前建筑墙体砌砖完成后,批刮一道混凝土砂浆扫平,然后直接粘贴建筑墙面砖,或批刮二道建筑腻子后进行涂刷建筑涂料。这种墙体处理方法存在如下问题(1)透气性差,墙体内外水蒸汽聚集不均匀,容易造成渗透现象。(2)墙体柔韧性差,易造成裂缝、龟裂。(3)导热系数大,夏天不隔热,冬天不保温。(4)相邻材料的导热系数偏差过大,导致墙体使用材料易脱落。
技术实现思路
本专利技术的目的就在于提供一种结晶型耐水保温抗裂高效胶泥,解决了现有技术的上述问题。本专利技术采用如下技术方案一种结晶型耐水保温抗裂高效胶泥,由胶粉和保温隔热粒料按每100公斤胶粉用480~600升保温隔热材料混合成,所述胶粉由下述重量份数的原料组成425#水泥550~625份石英砂 175~250份重质碳酸钙150~160份灰钙粉85~100份纤维素4~7份聚丙烯单丝纤维3~5份可再分散乳胶粉21~29份水泥基渗透结晶活性母料13~17份。本专利技术的这种结晶型耐水保温抗湿抗裂高效胶泥具有如下特点(1)具有较好的透气性。(2)导热系数小,防火性能达到B1级,具有很好的隔热性能,夏天隔热冬天保暖。(3)能够柔韧释放应力,解决了热胀冷缩引起的墙体裂缝、龟裂、脱落等现象。(4)系统综合粘接强度大于0.1Mpa,施工整体性好,柔性构造,抗冲击性大于3级。具体实施例方式下面结合具体实施例对本专利技术作进一步说明。实施例1采用425#硅酸盐水泥600公斤石英砂200公斤重质碳酸钙155公斤灰钙粉90公斤纤维素5公斤聚丙烯单丝纤维 4公斤可再分散乳胶粉 ...
【技术保护点】
一种结晶型耐水保温抗裂高效胶泥,其特征在于:由胶粉和保温隔热粒料按每100公斤胶粉用480~600升保温隔热材料混合成,所述胶粉由下述重量份数的原料组成:425#水泥550~625份,石英砂175~250份,重质碳酸 钙150~160份,灰钙粉85~100份,纤维素4~7份,聚丙烯单丝纤维3~5份,可再分散乳胶粉21~29份,水泥基渗透结晶活性母料13~17份。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。