本发明专利技术公开了一种水硬性调制磷铝酸盐彩色水泥，其各组分按重量百分比的含量是：磷铝酸盐水泥，８５．０－９２．０；活化硅质矿物，５．０－８．０；憎水剂，０．８－２．０；无机颜料，１．０－８．０。本发明专利技术的主要组分是低碱性的磷铝酸盐水泥，其硬化浆体水化产物不含Ｃａ（ＯＨ）↓［２］，浆体表面水化产物结构能固溶多种阴、阳离子或离子团，如：Ｎａ↑［＋］，ＣＯ↓［３］↑［２－］和ＳＯ↓［４］↑［２－］等，可以抑制泛碱；其硬化浆体色泽好，色牢度较高，大于８．０，而且改善了水泥混凝土的强度和耐久性。这种性能上的改善优于国内外现有的其它水硬性彩色胶凝材料。

A hard water modulated phosphor aluminate color cement

The invention discloses a hydraulic phosphoaluminate cement color modulation, the components according to weight percentage: 85 to 92 of phosphoaluminate cement; activation of siliceous minerals, 5 - 8; 0.8 - 2; hydrophobic agent, inorganic pigment, 1 - 8. The main component of the invention is low alkaline cement, its hardened paste hydration products containing Ca (OH): 2, the slurry surface structure of hydration products can dissolve a variety of anion and cation or ion clusters, such as: Na =, + 3, CO down arrow 2 - and 4 SO down arrow 2 negative, can inhibit the efflorescence; hardening slurry with good color, high color fastness, more than 8, but also improves the strength and durability of cement concrete. This improvement in performance is superior to other existing hydraulic color cementing materials at home and abroad.

【技术实现步骤摘要】
一种水硬性调制磷铝酸盐彩色水泥本专利技术属于无机材料领域，涉及一种能水化硬化的可用于建筑装 饰的特种胶凝材料，特别涉及一种水硬性调制磷铝酸盐彩色水泥。本专利技术要解决的技术问题是提供一种硬化浆体色泽好，色牢度较高，而且水泥砂浆的强度较高的7jC硬性调制磷铝酸盐彩色水泥。本专利技术的技术方案是， 一种水硬性调制磷铝酸盐彩色水泥，其组分按重量百分比的含量是活化硅质矿物5. 0-8. 0;憎水剂0. 8-2. 0;无机颜料1. 0-8. 0。以上所述的水硬性调制磷铝酸盐彩色水泥，所采用的活化硅质矿 物可以是焙烧白色苏州土、焙烧叶腊石、硅溶胶或硅凝胶中的一种或 其组合；所述的憎水剂可以是磷酸铝/磷酸铁、硬脂酸盐、脂肪酸、丙 烯酸酯中的一种或其组合。以上所述的水硬性调制磷铝酸盐彩色水泥，其各组分按重量百分 比的含量可以是磷铝酸盐水泥 88. 0-92. 0;氧化铬绿色颜料 2. 0-5. 0;焙烧叶腊石 6. 0-7. 5;磷酸铝/磷酸铁 Q. 8-1. 2。其各组分按重量百分比的含量也可以是磷铝酸盐水泥 85. 0-88. 0;氧化铁黄色颜料 5. 0-8. 0;硅凝胶 6. G-8. 0本文档来自技高网...

【技术保护点】
一种水硬性调制磷铝酸盐彩色水泥，其特征在于，其各组分按重量百分比的含量是：磷铝酸盐水泥８５．０－９２．０；活化硅质矿物５．０－８．０；憎水剂０．８－２．０；无机颜料１．０－８．０。

【技术特征摘要】

【专利技术属性】
技术研发人员：丁铸，邢锋，胡佳山，刘飚，李仕群，
申请(专利权)人：深圳大学，
类型：发明
国别省市：94[中国|深圳]