Non weathered cement mortar composition

The invention provides a dry mortar composition or water mortar composition form does not contain silica materials not weathered cement mortar composition, including: a) with cement mortar composition of dry weight of 1 to 10 weight percent of ordinary Portland cement, b) with cement mortar composition dry calcium aluminate cement weight of 1 to 30 wt.%, C) on a dry weight of calcium sulfate 1 to 15 wt.% of cement mortar composition, and D) a polymer powder with cement mortar composition of the dry weight of 0.5 aqueous polymer to 30 wt.% of dispersion or water dispersible these polymers, with one or more monomers based on these monomers selected from vinyl ester, (methyl) acrylate and vinyl aromatic compounds and olefins Classes, 1, 3 - dienes, and vinyl halides, and other monomers that may be polymerized with, if necessary.

【技术实现步骤摘要】
【国外来华专利技术】

【技术保护点】
一种干燥砂浆组合物形式或含水砂浆组合物形式的不含活性硅石材料的不风化的水泥砂浆组合物，其中包括：ａ）以水泥砂浆组合物的干重量计１重量％至１０重量％的普通波特兰水泥，ｂ）以水泥砂浆组合物的干重量计１重量％至３０重量％的铝酸钙水 泥，ｃ）以水泥砂浆组合物的干重量计１重量％至１５重量％的硫酸钙，及ｄ）以水泥砂浆组合物的干重量计０．５重量％至３０重量％的含水聚合物分散体或水中可再分散的聚合物粉末，这些聚合物以一种或多种单体为基础，这些单体选自乙烯基酯、（ 甲基）丙烯酸酯、乙烯基芳族化合物、烯烃、１，３－二烯以及乙烯基卤化物，以及如果需要，可与之共聚合的其他单体。

【技术特征摘要】
【国外来华专利技术】...

【专利技术属性】
技术研发人员：张明良，张杰，
申请(专利权)人：瓦克化学有限公司，
类型：发明
国别省市：DE[德国]