本发明专利技术公开了一种干粉界面处理剂，它是由以下重量份的原料组成的：４２５＃普通硅酸盐水泥５００份、２０－５０目的级配干沙４００份、７０－１４０目的级配干沙１００份、羟乙基纤维素２－３份、可再分散乳胶粉１０－２０份、甲酸钙２－３份。本发明专利技术的干粉界面处理剂通过添加有效量的胶粘剂使粘结强度提高，不空鼓、不开裂，可塑性大，适用于各种墙材的抹面，大大提高相互间的粘结力。通过添加有效量的保水剂和早强剂增加了它的保水性，不至于失水过快而影响强度，提高了早期强度，缩短了施工周期，克服了传统普通砂浆粘结层开裂、空鼓、脱落、渗漏等一系列质量问题。

Dry powder interface treatment agent

The invention discloses a dry interface treatment agent, which is composed of the following raw materials in weight portion: 425 ordinary portland cement 500, 20 - 50 to 400, 70 of dry sand gradation 140 objective gradation dry sand 100, 2 - 3 hydroxyethyl cellulose redispersible emulsion powder, 10 20, 2-3 copies of calcium formate. Dry interface treatment agent of the invention by adding an effective amount of the adhesive bond strength, no hollowing, cracking, plasticity, applicable to all kinds of wall plastering, greatly improve the adhesive force between each other. By adding an effective amount of water retaining agent and early strength agent to increase the water holding it, not excessive water loss and impact strength, improve the early strength, shorten the construction period, to overcome the traditional mortar bonding layer cracking, hollowing, shedding, leakage and a series of quality problems.

【技术实现步骤摘要】

【技术保护点】
一种干粉界面处理剂，它是由以下重量份的原料组成的：４２５＃普通硅酸盐水泥５００份、２０－５０目的级配沙４００份、７０－１４０目的级配沙１００份、保水剂２－３份、胶粘剂１０－２０份、早强剂２－３份；所述的保水剂为羟乙基纤维素； 所述的胶粘剂为可再分散乳胶粉；所述的早强剂为甲酸钙。

【技术特征摘要】

【专利技术属性】
技术研发人员：董志强，董斌，董杰，
申请(专利权)人：肥城润东建材有限公司，
类型：发明
国别省市：37[中国|山东]