A method for preparing high performance Mn Zn ferrite material, the invention uses MnZn ferrite wastes as raw materials, prepared by carbonate initial magnetic permeability of MnZn ferrite material R13K co precipitation, the Mn Zn ferrite wastes by sulfuric acid leaching, leaching solution and carbonate salt or alkali reduction as precipitant. To get the MnZn ferrite composite powder with co precipitation, the co precipitation powder by calcining, crushing, granulating, shaping and sintering atmosphere of initial magnetic permeability of MnZn ferrite R13K body. The invention has the advantages of simple process, high yield, good performance and no need to adjust the ceramic process, and has good popularization and application value.
【技术实现步骤摘要】
本专利技术涉及，具体地说是 以锰锌铁氧体废料为原料，采用碳酸盐共沉淀法制备初始磁导率为R13K的锰锌铁氧体材料的方法。
技术介绍
随着通讯、计算机网络等信息产业的发展，高性能锰锌铁氧体制 备成为磁性材料研究的前沿课题。检索国内外文献，高性能锰锌铁氧 体制备的研究重点大都集中在陶瓷法工艺。即以高纯Fe203、Mn304 和ZnO为原料，经过配料、 一次球磨、 一次造粒和预烧等工艺得到 锰锌铁氧体粉料，再经二次球磨、掺杂、二次造粒、成型和烧结等过 程制备铁氧体产品。其突出优点是工艺简单，但原料混合不充分和产 品稳定性差是陶瓷法难以克服的缺点。随着锰锌铁氧体应用领域的拓 展和材料开发的深化，IT产业及网络通讯等高端用户提出更高的要 求，陶瓷法制备技术难度更大。为克服这种不足，目前有多种新的锰 锌铁氧体粉料制备方法，如化学共沉淀法、水热法、溶胶-凝胶法、 超临界法、喷雾热解法、自蔓延高温合成法、低温合成法、微乳法和 共晶法等，其中仅有碳酸盐沉淀法实现工业应用。该方法采用高纯金属或化合物为原料，成本高，大规模工业推广难度大，这是陶瓷法迄 今仍占据市场绝对主导地位的根本原因...
【技术保护点】
一种高性能锰锌铁氧体材料的制备方法，其特征在于：将锰锌铁氧体废料经硫酸强化浸出、浸出液还原和碳酸盐或碱液作沉淀剂进行共沉淀得到锰锌铁复合粉料，将共沉淀粉经预烧、粉碎、造粒、成型和气氛烧结制得初始磁导率为Ｒ１３Ｋ的锰锌铁氧体。
【技术特征摘要】
【专利技术属性】
技术研发人员：彭长宏，唐谟堂，黄虹，李景芬，
申请(专利权)人：中南大学，
类型：发明
国别省市：43[中国|湖南]