The present invention relates to a containing alpha silicon nitride whisker silicon nitride slurry, the solid content is 15 ~ 40%, and the mass ratio of components which contain: alpha silicon nitride whisker from 1 to 10%, silicon nitride powder 16 ~ 25%, 1 ~ 8% polyvinyl alcohol polyethylene imine, 20 ~ 35%. Propylene glycol is 1 ~ 8%, the balance of deionized water. The preparation method of the slurry is: adding alpha silicon nitride whiskers, with deionized water as a solvent, using polyethyleneimine as dispersing agent, PVA as binder, propylene glycol as a plasticizer; adding four methyl ammonium chloride to adjust the pH value of the slurry; preparation method comprises the following steps of proportioning, mixing, milling two times and the postprocessing procedure. The slurry with low viscosity, high whisker content and good dispersion, suitable for tape casting; use the film surface slurry preparation, powder particles and uniform pore size distribution, high strength, good manufacturability; and simple preparation technology, low cost, short cycle.
【技术实现步骤摘要】
本专利技术涉及一种水基流延浆料及其制备方法，特别是涉及一种含有a-氮化硅晶须的氮化 硅水基流延浆料及其制备方法。技术背景氮化硅是无机非金属强共价键化合物，由于氮原子之间结合得非常牢固，具有高比强、 高比模、耐高温、抗氧化和耐磨损以及高抗热震性等优点，所以在高温、高强腐蚀介质的工 作环境中具有特殊的使用价值。氮化硅结构陶瓷材料虽然具有以上许多优异的性能，且在各领域中有广泛的重要应用，但是它的致命的弱点脆性，还是会阻碍它的更广泛的应用，它 不像金属那样具有塑性变形的能力，具有可滑移的位错系统，当外加能量超过一定的限度时， 它只有形成新的表面来消耗外加能量，即在陶瓷体内形成新的裂纹表面导致灾难性的破坏。目前，氮化硅结构陶瓷的增韧途径主要有颗粒增韧、晶须或纤维增韧、Zr02相变增韧及 柱状/3-Si3N4晶粒的自增韧等四种途径。其中，晶须是在人工控制的条件下合成的一种高强度 胡须状的单晶体，其晶体结构比较完整，内部缺陷少，其强度和模量均接近理想晶体，因此， 常将其作为增强组元加入到金属基、陶瓷基和高分子基材料中起增强、增韧作用。20世纪80年代中期晶须增强增韧复合材...
【技术保护点】
一种氮化硅水基流延浆料，其特征是一种含有α－氮化硅晶须的氮化硅水基流延浆料，该料浆的固相含量为１５～４０％，该浆料所含的组分及其质量配比为：α－氮化硅晶须１～１０％，氮化硅粉体１６～２５％，聚乙烯亚胺１～８％，聚乙烯醇２０～３５％，丙二醇１～８％，去离子水余量。
【技术特征摘要】
【专利技术属性】
技术研发人员：张联盟，李君，陈斐，刘晶，张东明，沈强，王传彬，
申请(专利权)人：武汉理工大学，
类型：发明
国别省市：83[中国|武汉]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。