The invention relates to a dewatering sludge produced by the solidification / stabilization treatment with curing agent, which is characterized in that the dewatered sludge according to the weight proportion adding curing materials and auxiliary curing materials of bentonite, the components are mixed evenly, each component weight percentage: 30 to 80% sludge solidification material 15. ~ 30%, 5 ~ 40% bentonite; the curing material consists of cement, lime, fly ash and gypsum, according to a certain weight ratio. Advantages: the treated sludge can be disposed of and recycled as a soil material. The curing agent can improve the high water content and low strength property of the sludge, and has the advantages of improving the curing effect, reducing the dosage of the curing material and reducing the treatment cost. The composition of curing agent, cement, fly ash, lime, gypsum and bentonite are widely distributed, low price, finished products are sold, and the industrialization of sludge solidification / stabilization treatment technology can be realized.
【技术实现步骤摘要】
本专利技术涉及的是一种对污水厂产生的脱水污泥进行固化/稳定化处理时 所使用的固化剂。通过这种固化剂进行固化/稳定化处理后的污泥可以满足 填埋处置的要求，也可用作为一般的土材料进行使用，属于资源环境领域。
技术介绍
目前污泥的处置主要以转为农用、焚烧处理和填埋场填埋为主。污泥中 的重金属超标限制了污泥农用。焚烧处理投资及运行费用较大。将污泥送往 卫生填埋场进行填埋处置，由于污泥的含水率高、力学性质差，未经处理的污泥直接进入填埋场往往会引起滑坡等填埋场的工程灾害。污泥由于含水率 高，有机物含量高，无机固体颗粒成分少，固化/稳定化处理后所形成的强 度主要是依靠水泥水化反应形成的水化产物，这样就需要消耗大量的水泥才 能获得一定的强度，所以其处理费用较高。
技术实现思路
本专利技术的目的是为解决污水处理中产生的大量污泥，对其进行固化/稳 定化处理用固化剂，处理后的污泥能够满足填埋处置或资源化利用的要求。本专利技术的技术方案其特征是在脱水污泥中按重量比例添加固化材料辅 助固化材料膨润土，将各组分混合搅拌均匀，各组分所占重量百分比为污泥 30 80%， 固化材料 15 30%...
【技术保护点】
污水厂产生的脱水污泥进行固化／稳定化处理用固化剂，其特征是在脱水污泥中按重量比例添加固化材料和辅助固化材料膨润土，将各组分混合搅拌均匀，各组分所占重量百分比为：污泥３０～８０％，固化材料１５～３０％，膨润土 ５～４０％；上述的固化材料由水泥、石灰、粉煤灰以及石膏，各组成成分质量比为水泥∶石灰∶粉煤灰∶石膏＝（１３－１８）∶（１－４）∶（１－３）∶（１－３）。
【技术特征摘要】
【专利技术属性】
技术研发人员：朱伟，李磊，张春雷，林城，
申请(专利权)人：河海大学，
类型：发明
国别省市：84[中国|南京]