The invention relates to a method for preparing solid waste fired ceramsite, which belongs to the field of building materials. The present invention uses coal gangue, sludge and waste glass powder as raw materials to bake high-performance ceramsite products. The percentage of the components in the formula is 15 to 45% of the gangue, 25% to 50% of the municipal dry sludge, and 20% to 50% of the waste glass powder. According to the above formula green ceramsite prepared after drying at 300 DEG C to 600 DEG C for 20 to 50 minutes of low carbon, 950 to 1100 DEG C for 8 to 20 minutes of firing, product performance obtained with ceramsite lightweight \GB / T17431.11998 standard material and its test method\.
【技术实现步骤摘要】
一种利用煤矸石、污泥和废玻璃粉烧制轻质高强陶粒的制备方法，属于 建筑材料
技术背景煤矸石是我国目前排放量最大的固体废弃物，其产量占原煤总产量的15% 20%，目前我国己积存50亿吨，而且以年排放量1.5亿吨的速度快速 增长。我国年产干污泥量约为50万吨，目前主要以填埋为主。煤矸石和污泥 的堆放和填埋，不仅占有了大量的土地，并且造成了巨大的环境污染，急需 加以无害化处理。陶粒作为一种建筑材料，可以大量消耗不能降解的无机非 金属质固体废弃物，为处理这些固体废弃物提供了一个有效的手段。现有煤矸石陶粒在成型过程中需要加入粘结剂(粘土、聚乙烯醇等)， 一般烧制温度在IIO(TC以上。现有污泥陶粒也要加入粘土等提高制品强度的 天然矿物，烧制温度均在105(TC以上，有的甚至在125(TC时烧成。而玻璃陶 粒的制备过程中，由于玻璃粉是瘠性料、可塑性差，在成型过程中需要使用 粘结剂、改性剂和发泡剂，才能烧制轻质陶粒。
技术实现思路
本专利技术以现有的污泥陶粒、煤矸石陶粒和玻璃陶粒制造技术为基础，是 这些技术的发展。本专利技术以煤矸石、回收废玻璃粉和污泥作为主要原料，制 ...
【技术保护点】
一种固体废弃物烧制陶粒的制备方法，其特征在于，包括如下步骤：（１）以煤矸石、城市污水处理厂脱水生活污泥和回收废玻璃为原料，各组成质量百分比如下所示：煤矸石１５％～４５％，城市生活干污泥２５％～５０％，废玻璃粉２０％～５０％； （２）将各种原料以上述比例加入到预混搅拌机中搅拌，同时以喷雾形式加入水，最终水分质量百分比含量为上述原料和水分总质量的２０％～３０％；搅拌均匀后，将混合好的原料送入造粒机造粒；然后将陶粒生坯放入烘箱中充分干燥；（３）低温保温排炭阶段 ：３００℃～６００℃保温２０～５０分钟；室温至所选定的低温保温温度为以２０℃...
【技术特征摘要】
【专利技术属性】
技术研发人员：严建华，王亚丽，王峰，崔素萍，兰明章，王子明，李智丰，
申请(专利权)人：北京工业大学，
类型：发明
国别省市：11[中国|北京]