Technology for preparation of fly ash fiber sheet, which is characterized in that the first preparation of water repellent agent solution, the method is: water is heated to a certain temperature, the ethylene glycol butyl ether is added to the heated water, the organic acid is added to the heated water, stirring to completely dissolve organic acid, the water resistance agent solution. Then the fly-ash fiber is heated to 100-150 degrees, then evenly sprayed acrylic resin emulsion on it, to continue in the hot pressing temperature and pressure, get the fly ash fiber sheet, and then into the oven plate 100-150 DEG C in this temperature, anti water solution is uniformly sprayed to fly ash fiber sheet, drying to obtain the final fly ash fiber sheet. The fly ash fiber board prepared by the technique has the advantages of light weight, good water resistance and good flame retardance, and can be used as building materials and is used for heat preservation of suspended ceiling and internal and external walls.
【技术实现步骤摘要】
本专利技术涉及一种粉煤灰纤维板材的制备技术，具体地说，是用乳液 作粘接剂来制备粉煤灰纤维板材，再对粉煤灰纤维板材表面进行抗水处理 的工艺方法。技术背景粉煤灰纤维是近年来发展的一种混杂无机氧化物纤维。粉煤灰是我国 最大的工业废渣和排放物，主要来源于燃烧高炉及火力发电的燃烧残余物，每年逾越6亿吨。粉煤灰的主体化学成份为Si02、 A1203、 CaO、 Fe203以及 少量的Ti02、 MgO。其大部分元素与原始矿产物质所含元素相同。随着工 业的长期开发和使用，矿产天然资源已日渐枯竭，而煤炭燃烧废弃物粉煤 灰却日渐增多，堆积成忧。因此，利用粉煤灰的化学成份及结构特性，将 其深加工转化成工业应用原料，代替部分天然矿物资源，是近年研究者兴 趣的课题之一。将粉煤灰制备成具有高价值的超细无机纤维，进而利用纤 维实现多种用途制造纸桨用于生产纸板纸品；制造保温隔音隔热材料和 节能墙体材料；制造轻质阻燃建筑屋吊顶；制造纤维增强树脂复合材料； 用于工业过滤材料；用于改善国产沥青低温开裂、高温软化的劣性等。粉煤灰可在无机助熔剂(菱镁矿、白云石、石灰石等)以及废碎玻璃的搭配下，通过...
【技术保护点】
一种粉煤灰纤维板材的制备技术，其特征在于，先制备抗水剂溶液，其方法为：将水加热到一定的温度，将乙二醇丁醚加入到加热水中，再将有机酸加入到加热水中，搅拌使有机酸完全溶解，得到抗水剂溶液。然后将粉煤灰纤维加热到１００－１５０℃，在其上均匀地喷洒丙烯酸类树脂乳液之后，继续在该温度和一定的压强下进行热压成型，得到粉煤灰纤维板材，再将板材放入１００－１５０℃的烘箱中，在此温度下将抗水剂溶液均匀地喷洒到粉煤灰纤维板材上，干燥后即得到最终的粉煤灰纤维板材。
【技术特征摘要】
【专利技术属性】
技术研发人员：陈建定，王彦华，夏浙安，
申请(专利权)人：华东理工大学，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。