The invention relates to a method for preparing alpha hemihydrate gypsum by using desulfurized gypsum. The technical scheme is: first or will desulfurization gypsum slurry concentration and complete oxidation of 2 ~ 60wt% salt solution according to the mass ratio of 0.2 to 1.5: 1 were mixed in a slurry tank, or solid gypsum and salt solution concentration was 2 ~ 35wt% according to the mass ratio of 0.2 to 1: 1 mixed in the mixing tank, regulating slurry mixture of pH value to 3 ~ 8. Then the slurry was fed into the mold and stirred at 0.3 ~ 12hr at a temperature of 80~110. Then, the crystallized slurry is fed into a mature tank and stirred at 0.2 DEG 4hr at a temperature of 80~110 DEG C. Finally, the matured slurry is washed and dried by solid-liquid separation to obtain alpha - hemihydrate gypsum. The invention can be intermittent or continuous operation, wide application range; atmospheric transformation, save the investment cost and operation cost, increase reliability; low temperature salt solution conversion, does not require expensive steam as a heat source, can reduce the production cost.
【技术实现步骤摘要】
本专利技术涉及一种用脱硫石膏制备(x-半水石膏的方法。尤其是涉及一种基于低温盐溶液法 用脱硫石膏制备a-半水石膏的方法。
技术介绍
烟气脱硫(FGD)技术的应用是控制酸雨污染的有效途径，其中钙基湿法烟气脱硫工艺是 目前世界上唯一大规模应用的烟气脱硫工艺，在该烟气脱硫工艺中产生以CaSCV2H20为主 要成分的脱硫渣，俗称脱硫石膏。实现脱硫石膏资源化利用，才能从根本上解决SCb污染问 题，增加烟气脱硫方法的选择空间，提升湿法烟气脱硫的技术水平，扩展工艺发展的环境容 量，实现"资源一产品一废物排放与末端治理"向"资源一产品一再生资源与回用"模式的转变， 促进脱硫事业的良性循环；还有利于保护自然资源，减少因矿物开采和运输过程对生态环境 的破坏和污染，对实现国民经济的可持续发展具有重要意义。脱硫石膏的主要成分为CaS04，2H20，不能满足应用需要。在石膏的5种晶体形态中，以 半水石膏为原料制备的石膏产品应用广泛。因此需要对脱硫石膏进行改性，达到应用的要求。 在半水石膏中，a-半水石膏是一种性能优良的改性石膏，具有需水量少，强度高等优点，因 此利用技术手段实现脱硫石膏转...
【技术保护点】
一种用脱硫石膏制备α－半水石膏的方法，其特征在于或先将完全氧化的脱硫石膏浆液与浓度为２～６０ｗｔ％的盐溶液按质量比为０．２～１．５∶１在配浆罐进行混合，或先将固体脱硫石膏与浓度为２～３５ｗｔ％的盐溶液按质量比为０．２～１∶１在配浆罐进行混合，调节混合后的浆液ｐＨ值至３～８；再将调节后的浆液送入结晶器中，在温度为８０～１１０℃条件下搅拌０．３～１２ｈｒ；然后将结晶后的浆液送入熟化罐，在温度为８０～１１０℃的条件下搅拌０．２～４ｈｒ；最后对熟化后的浆液经固液分离后进行洗涤和干燥。
【技术特征摘要】
【专利技术属性】
技术研发人员：吴晓琴，童仕唐，何伟，张春桃，吴忠标，官宝红，
申请(专利权)人：武汉科技大学，
类型：发明
国别省市：83[中国|武汉]