92%低温Al*O*瓷粉制造技术

本发明专利技术提供一种９２％低温Ａｌ↓［２］Ｏ↓［３］瓷粉，按重量百分比计，该瓷粉由以下组分组成：α－Ａｌ↓［２］Ｏ↓［３］　９０％～９３％，高岭土３％～６．５％，方解石２％～４．５％，煅烧滑石０．３％～０．７％，ＺｎＯ　０．３％～０．５％、ＣｅＯ↓［２］　０．３％～０．６％、ＭｇＴｉＯ↓［２］　０．３％～０．５％；所述α－Ａｌ↓［２］Ｏ↓［３］纯度≥９９．７％，其平均粒径２～５μｍ；采用本发明专利技术所述９２％低温Ａｌ↓［２］Ｏ↓［３］瓷粉可降低Ａｌ↓［２］Ｏ↓［３］陶瓷的烧结温度，还可提高Ａｌ↓［２］Ｏ↓［３］陶瓷的烧成密度，且有利于节能减排。

92% low temperature Al*O* porcelain powder

The invention provides a low temperature 92% Al: 2 O: 3 ceramic powder according to the weight percentage, the ceramic powder is composed of the following components: alpha Al: 2 O: 3 90% ~ 93%, 3% ~ 6.5% calcite 2% kaolin, calcined talc 0.3% ~ ~ 4.5%. 0.7%, ZnO 0.3% ~ 0.5%, CeO: 2, MgTiO: 0.3% ~ 0.6% 2 0.3% ~ 0.5%; the alpha Al: 2 O: 3. The purity of more than 99.7%, the average particle size of 2 to 5 mu m; sintering temperature of the low temperature Al: 92% 2: O 3 ceramic powder can reduce Al: 2 O: 3 Ceramics, which can improve the Al down 2, down O 3) the firing density of the ceramic is favorable for energy conservation and emission reduction.

【技术实现步骤摘要】

本专利技术涉及一种A 1 20 3陶瓷的烧结原料，具体地说，涉及了一种92% 低温A 1 20 3瓷粉。
技术介绍
A 1 2 0 3陶瓷是氧化物中化学性质最稳定、机械强度最高的 一 种 新型材料，其优点是具备优异的高温机械性能，耐化学腐蚀， 耐高温氧化，耐磨损，比重小(约为金属的1/3);因而，A"03陶 瓷在许多场合逐渐取代昂贵的超高合金钢，或被应用到金属材料 根本无法胜任的场合，如发动机气缸套、轴瓦、密封圏、纺织耐 磨零件、陶瓷切削刀具等；另外，A 1 20 3陶瓷具有优异的电绝缘性 能和较低的介质损耗等优点，因而，在电子、电器方面也有十分 广阔的应用领域，如今，Ah03陶瓷已广泛用于电子、电器、机械、 化工、纺织、冶金、医疗和航空航天等行业中。由于Ah03熔点高达2 05 0 °C ，导致A 1 20 3陶瓷的烧结温度普遍 较高，因此，如何能够在不影响陶瓷性能的前提下，降低A1203 陶瓷的烧结温度，降低能耗，缩短其烧成周期，减少窑炉和窑具 损耗，从而达到降低生产成本，对大部分陶瓷厂家来说是急需解 决的问题。树立科学发展观，节能减排、降低能耗，建设节约型社会是 十七大提出的本文档来自技高网...

【技术保护点】
一种９２％低温Ａｌ↓［２］Ｏ↓［３］瓷粉，其特征在于，按重量百分比计，该瓷粉由以下组分组成：α－Ａｌ↓［２］Ｏ↓［３］９０％～９３％，高岭土３％～６．５％，方解石２％～４．５％，煅烧滑石０．３％～０．７％，ＺｎＯ０．３％～０．５％、ＣｅＯ↓［２］０．３％～０．６％、ＭｇＴｉＯ↓［２］０．３％～０．５％。

【技术特征摘要】

【专利技术属性】
技术研发人员：黄超，张莎莎，朱宁宁，
申请(专利权)人：黄超，
类型：发明
国别省市：41[中国|河南]