一种由脱炭粉煤灰生产的地面砖及其制备方法技术

本发明专利技术公开了一种由脱炭粉煤灰生产的地面砖及其制备方法，先将脱炭粉煤灰、水泥、粗骨料、生石灰和活性激发剂混合搅拌得到底料；再将白水泥、颜料和尾矿渣混合搅拌得到面料；然后将面料和底料混合、压模成型和养护后即得成品。本发明专利技术提供的粉煤灰地面砖具有生产成本低，生产工艺简单，有效解决了脱炭粉煤灰资源化问题，从环保、节约能源或资源利用来说，粉煤灰地面砖作为新颖的路面装饰材料，具有良好的社会效益和生态效益，具有广阔的市场前景，是一种有效的粉煤灰资源化利用途径。

Ground tile produced by removing carbon fly ash and preparation method thereof

The invention discloses a method for removing carbon from production of fly ash brick and its preparation, the first carbon removal of fly ash, cement, coarse aggregate, lime and activator mixing by bottom material; then the white cement, pigment and slag mixed by fabric; then surface material and base material mixing, compression molding and curing to obtain the finished product. Fly ash brick is provided by the invention has the advantages of low production cost, simple production process, effectively solves the problem of decarburized fly ash resources, from environmental protection, energy saving or resource utilization, fly ash brick as a novel pavement decoration material, has good social and ecological benefits, and has broad market prospects that is an effective way of utilization of fly ash resources.

【技术实现步骤摘要】

本专利技术涉及的是建筑领域的一种地面砖及其制备方法。
技术介绍
粉煤灰是生产粉煤灰地面砖主要原料之一。根据现有文献资料，王占魁采用电厂干排粉 煤灰制作彩色地面砖(粉煤灰综合利用1998年第1期)，黄江丽等采用热电厂粉煤灰制取彩 色地面砖，(中国资源综合利用2003/09)，这些粉煤灰生产彩色地面砖的方法是直接采用 从燃煤电厂排放的烧失量低于10%的粉煤灰，炭含量高的粉煤灰不能直接使用。
技术实现思路
本专利技术所要解决的技术问题是提供一种由脱炭粉煤灰生产地面砖的方法，直接将脱炭粉 煤灰和其它物料进行科学的原料配比和成型压力，使产品既有很高的强度又有理想的密实性为了解决上述问题，提供一种由脱炭粉煤灰地面砖本专利技术专利则是首先将烧失量为20-30%的高炭湿排粉煤灰按常规工艺进行脱炭，得到烧 失量低于10%的粉煤灰尾灰即脱炭粉煤灰作为原料制备粉煤灰地砖。该地面砖包括面料和底料，其中面料和底料的重量比为l: 3 l:8;底料的组成及重量百分比为脱炭粉煤灰为45 50%、水泥为13 19%、粗骨料为17 23%、生石灰为13 19%和活性激发剂为0. 3 0. 5%;面料的组成及重量百分比为本文档来自技高网...

【技术保护点】
一种由脱炭粉煤灰生产的地面砖，该地面砖包括面料和底料，其特征在于：面料和底料的重量比为１∶３～１∶８；　底料的组成及重量百分比为：脱炭粉煤灰为４５～５０％、水泥为１３～１９％、粗骨料为１７～２３％、生石灰为１３～１９％和活性激发剂为０．３～０．５％；　面料的组成及重量百分比为：白水泥为２５～３５％、颜料为５～２０％和尾矿渣为５０～７０％。

【技术特征摘要】

【专利技术属性】
技术研发人员：卯松，张覃，刘志红，唐云，邱跃琴，
申请(专利权)人：贵州大学，
类型：发明
国别省市：52[中国|贵州]