The invention of black glass ceramics is made of fly ash and borax factory and titanium dioxide plant residue as raw material, mix ingredients according to the weight of 8:3:0.5 production. The invention has the following components: SiO glass range 2 35 ~ 55%, Al 2 O 3 18 ~ 28%, 2 Fe O 3 FeO2 ~ 11%, CaO1 ~ 5%, MgO7 ~ 14%, K 2 ONa 2 O1 ~ 4%, TiO 2 0.5 - 5%, - 2 O 3 0.4 ~ 3%, P 2 O 3 0 ~ 1%. of the glass melting temperature 1450 + 20 DEG C, the annealing temperature is 650 DEG C for 4 hours, the crystallization temperature of 910 degrees. After the treatment of hard glass ceramics The degree of Damoshi grade 7 to more than 9 level.
【技术实现步骤摘要】
本专利技术涉及特种铸石的原料特征和材料成份组成。本专利技术的
属微晶玻璃。本材料试验成功前有熔铸辉绿岩等类似材料，但不属于微晶玻璃的范围。苏联专利SU-937375工业铸石的成份(Indus-trial Cast stone Composition)，SU-687011房屋工业用的耐磨铸石(Wear Resistant Cast stone for use in Building Industry)有参考作用。但微晶玻璃组成和粉煤灰废渣微晶玻璃的组成不同。铸石生产的不足之处是要用部分天然矿石作原料。本专利技术目的是用全部或接近全部粉煤灰等工业废渣，在生产各种产品的同时减少环境污染。本专利技术玻璃具有下列组成范围SiO235～55%，Al2O318～28%，Fe2O3+FeO 2～11%，CaO 1～5%，MgO 7～14%，K2O+Na2O 1～4%，TiO20.5～5%，B2O30.4～3%，P2O30～1%。本玻璃的原料重量配合比为粉煤灰∶硼砂厂废渣(含MgO 30～40%)∶钛白粉厂废渣(...
【技术保护点】
本专利技术的技术特征是以粉煤灰、硼砂厂和钛白粉厂的废渣为全部或接近全部原料。不用纯碱和矿石生产的黑色微晶玻璃，本玻璃经微晶化处理后硬度达莫氏７级至大于９级，请求保护范围：１、是以粉煤灰、硼砂厂和钛白粉厂废渣为主要原料制成的黑色微晶玻璃， 其组成范围为：ＳｉＯ↓〔２〕３５～５５％，Ａｌ↓〔２〕Ｏ↓〔３〕１８～２８％，Ｆｅ↓〔２〕Ｏ↓〔３〕＋ＦｅＯ２～１１％，ＣａＯ１～５％，ＭｇＯ７～１４％，Ｋ↓〔２〕Ｏ＋Ｎａ↓〔２〕Ｏ１～４％，ＴｉＯ↓〔２〕０．５～５％，Ｂ↓〔２〕Ｏ↓〔３〕０．４～３％，Ｐ↓〔２〕Ｏ↓〔３〕０～１％。该玻璃经微晶化处理后硬度达莫氏７级至大于９级。
【技术特征摘要】
本发明的技术特征是以粉煤灰、硼砂厂和钛白粉厂的废渣为全部或接近全部原料，不用纯碱和矿石生产的黑色微晶玻璃，本玻璃经微晶化处理后硬度达莫氏7级至大于9级。请求保护范围1、是以粉煤灰、硼砂厂和钛白粉厂废渣为主要原料制成的黑色微晶玻璃，其组成范围为...
【专利技术属性】
技术研发人员：陈聘珍，赵天佑，