一种新型绿色环保结晶玻璃板材的配方及生产技术组成比例

本发明专利技术公开了一种新型绿色环保结晶玻璃板材的基础配方、颜色系列、生产工艺及复合层板材制造技术，产品色彩绚丽，花纹层次感强、独具特色，性能优良。专有的复合层板材制造技术，用于生产贵妃红等高档板材，在不影响产品性能的前提下，大幅度降低了生产成本。本发明专利技术生产的结晶玻璃板材不含放射性元素，确保生态环境，属于新型绿色环保建材产品。（*该技术在2021年保护过期，可自由使用*）

Formulation and production technology of a new type of green environmental protection crystalline glass sheet

The invention discloses a formulation, the new green crystalline glass plate color series, the production process and the production technology of composite plate products, brilliant color, pattern of strong sense of hierarchy, unique, excellent performance. Proprietary composite laminated plate manufacturing technology, used in the production of red silk and other high-grade plate, without affecting the performance of the premise, greatly reducing production costs. The crystalline glass plate produced by the invention does not contain radioactive elements and ensures the ecological environment, and belongs to a new type of green environmental protection building material product. \ue5cf

【技术实现步骤摘要】

本专利技术涉及一种新型绿色环保结晶玻璃板材的配方及生产技术。国内现有微晶玻璃板材生产厂家生产的产品颜色品种单调，盲目追求结晶率，晶体数量多、长度短，外观无明显花纹效果，缺乏层次感，色泽黯淡，属中低档制品。本专利技术的新型绿色环保结晶玻璃板材颜色品种丰富，色彩斑斓，高贵典雅。通过控制生产工艺，如升温速度、结晶温度、保温时间、颗粒度等，控制晶核生成速度和晶体的生长速度，使晶相含量在45～65％，晶体生长到一定的长度，晶相和玻璃相互相映衬，花纹效果层次感强，美丽柔和，各项性能指标优于天然花岗岩板材，且不含放射性元素，确保生态环境，属于新型绿色环保建材产品。本专利技术的结晶玻璃板材由下列原料及组分制成(重量％)白色基料为石英粉35～50(砂岩40～55)，氧化铝1.5～7，纯碱5～15，氧化锌2～7，石灰石25～35，长石17～25，碳酸钡2～8；颜色品种系列在白色基料的基础上分别添加适量其它化工原料及着色剂，其中1、贵妃红 在白料基础上加氧化铜0～1，氧化亚铜1～2.5，锡粉2～7，碳粉0.5～1.5，硅粉0.2～1；2、灰色 在白料基础上加氧化铁0.8～2，氧化钴0.01～0.本文档来自技高网...

【技术保护点】
一种新型绿色环保结晶玻璃板材的基础配方，其特征在于玻璃成分为（重量％）：ＳｉＯ↓［２］５０～６９，Ａｌ↓［２］Ｏ↓［３］１．５～８，ＣａＯ５～１９，ＭｇＯ０．１～２，ＺｎＯ０．１～９，ＢａＯ１～７，Ｂ↓［２］Ｏ↓［３］０．１～２，Ｒ↓［２］Ｏ４～１２，Ｓｂ↓［２］Ｏ↓［３］０～１．５。